Bencze, Andrei (avtor), Bergant, Zoran (avtor), Arnăutu, Irina (avtor), Šturm, Roman (avtor), Chlada, Milan (avtor), Steigmann, Rozina (avtor), Stanciu, Mariana Domnica (avtor), Savin, Adriana (avtor)

Tailored flax-reinforced composites (TFRC) are being investigated as a sustainable alternative to conventional glass- and carbon-fiber-reinforced composites, having a lower fiber volume than these and the structure of the laminate with two plies (two identical layers of alkali-treated flax yarns) is unidirectional, weakly twisted, oriented at ±45°, and reinforced by stitching; it is also impregnated with bio-resin and has robust reinforcement through controlled lamination. TFRC has shear-dominated behavior under both tensile and compressive loading, due to the off-axis orientation of the fibers, but the damage evolution differs significantly. Under tensile loading, the material exhibits a lower strength (55.2 MPa), whereas under compression loading, the composite achieves a higher apparent strength (99.1 MPa). The paper provides a comprehensive analysis for structural and mechanical characterization using the following: nondestructive evaluation using ultrasound to detect internal discontinuities and assess homogeneity; optical microscopy to evaluate fiber–matrix integration and porosity reduction; and Dynamic Mechanical Analysis to assess thermomechanical transitions and storage modulus stability. Finite element simulations have been used to determine elastic properties and validate the matrix-dominated shear response. The results confirm that the [±45°]4S sequences of TFRC optimize mechanical response and interfacial adhesion, promoting TFRC as an ecological solution for structural systems where progressive energy dissipation is preferred.

• Jezik: Angleški jezik
• Ključne besede: biocomposites, flax fibers, flax-reinforced composites, sustainability, mechanical properties, dynamic mechanical analysis
• Vrsta gradiva: Članek v reviji
• Tipologija: 1.01 - Izvirni znanstveni članek
• Organizacija: FS - Fakulteta za strojništvo
• Status publikacije: Objavljeno
• Različica publikacije: Objavljena publikacija
• Leto izida: 2026
• Št. strani: 28 str.
• Številčenje: Vol. 18, issue 17, art. 2069
• PID: 20.500.12556/RUL-186063
• UDK: 66.02
• ISSN pri članku: 2073-4360
• DOI: 10.3390/polym18172069
• COBISS.SI-ID: 288947971
• Datum objave v RUL: 26.08.2026

Gradivo je del revije

• Naslov: Polymers
• Skrajšan naslov: Polymers
• Založnik: MDPI
• ISSN: 2073-4360
• COBISS.SI-ID: 517951257

Licence

• Licenca: CC BY 4.0, Creative Commons Priznanje avtorstva 4.0 Mednarodna
• Povezava: http://creativecommons.org/licenses/by/4.0/deed.sl
• Opis: To je standardna licenca Creative Commons, ki daje uporabnikom največ možnosti za nadaljnjo uporabo dela, pri čemer morajo navesti avtorja.

Sekundarni jezik

• Jezik: Slovenski jezik
• Ključne besede: biokompoziti, lanena vlakna, kompoziti, trajnost, dinamična mehanska analiza