Effects of airborne-particle abrasion and zirconia composition on porcelain–zirconia bond strength

Antanasova, Maja (avtor), Malgaj, Tine (avtor), Drev, Sandra (avtor), Vukšić, Milan (avtor), Jevnikar, Peter (avtor), Kocjan, Andraž (avtor)

Porcelain chipping in zirconia-based dental restorations remains a major clinical complication. This study evaluated the effects of airborne-particle abrasion (APA) and yttria content in zirconia on porcelain–zirconia bond strength. Six groups were tested: low-translucency (3Y-TZP) and high-translucency zirconia (4Y-TZP), each with or without APA, and APA-treated Co–Cr and Ti–6Al–4V alloys as metal–ceramic references. Bond strength was assessed using the Schwickerath test. Interfacial structure and mechanical properties were analyzed by scanning and transmission electron microscopy and nanoindentation. APA significantly increased zirconia surface roughness but did not improve bond strength. Zirconia composition had no effect on porcelain bonding. Bond strength values for porcelain-zirconia (34.0–40.6 MPa) were comparable to those of metal–ceramic systems, lower than Co–Cr (45.5 MPa) but similar to Ti–6Al–4V (37.3 MPa). Microscopy and nanoindentation revealed sharp zirconia–porcelain interfaces with pronounced mechanical mismatch and yttrium segregation at grain boundaries.

• Jezik: Angleški jezik
• Ključne besede: airborne-particle abrasion, Yttria-stabilized zirconia (Y-TZP), zirconia-based ceramics
• Vrsta gradiva: Članek v reviji
• Tipologija: 1.01 - Izvirni znanstveni članek
• Organizacija: MF - Medicinska fakulteta
• Status publikacije: Objavljeno
• Različica publikacije: Objavljena publikacija
• Leto izida: 2026
• Št. strani: 10 str.
• Številčenje: Vol. 26, art. 100980
• PID: 20.500.12556/RUL-184435
• UDK: 620.1/.2
• ISSN pri članku: 2666-5395
• DOI: 10.1016/j.oceram.2026.100980
• COBISS.SI-ID: 278157059
• Datum objave v RUL: 07.07.2026

Gradivo je del revije

• Naslov: Open ceramics
• Založnik: Elsevier
• ISSN: 2666-5395
• COBISS.SI-ID: 25023747

Licence

• Licenca: CC BY 4.0, Creative Commons Priznanje avtorstva 4.0 Mednarodna
• Povezava: http://creativecommons.org/licenses/by/4.0/deed.sl
• Opis: To je standardna licenca Creative Commons, ki daje uporabnikom največ možnosti za nadaljnjo uporabo dela, pri čemer morajo navesti avtorja.

Sekundarni jezik

• Jezik: Slovenski jezik
• Ključne besede: zrak, abrazija delcev, keramika, cirkonij

Projekti

• Financer: ARIS - Javna agencija za znanstvenoraziskovalno in inovacijsko dejavnost Republike Slovenije
• Številka projekta: P2-0087
• Naslov: Keramični in komplementarni materiali za napredne inženirske in biomedicinske aplikacije

• Financer: ARIS - Javna agencija za znanstvenoraziskovalno in inovacijsko dejavnost Republike Slovenije
• Številka projekta: Z3-70130
• Naslov: Biofunkcionalizacija cirkonijevih oksidnih opornikov za izboljšanje peri-implantatnega zdravja: Aditivni hierarhični pristop strukturiranja površine
• Akronim: BioZIR