Microstructure and properties after friction stir processing of twin-roll cast Al–Mn–Cu–Be alloy

Macerl, Matjaž (avtor), Zupanič, Franc (avtor), Hočuršćak, Lara (avtor), Klobčar, Damjan (avtor), Kovács, Andras (avtor), Bončina, Tonica (avtor)

We studied the effect of friction stir processing (FSP) on the microstructure and properties of high-speed twin-roll cast strips made of an experimental Al–Mn–Cu–Be alloy. The samples were examined using light, scanning, and transmission electron microscopy, microchemical analysis, X-ray diffraction, and indentation testing. During FSP, the rotational speed varied, while other parameters remained constant. The uniformity of the microstructure increased with the growing rotational speed. In the stir zone, several processes took place, and the most important were: recrystallisation of the matrix grains, fragmentation of the primary intermetallic particles Al▫$_{15}$▫Mn▫$_{3}$▫Be▫$_{2}$▫ and their more uniform distribution in the stir zone, fracture, and dispersion of the eutectic icosahedral quasicrystalline phase (IQC), transformation of tiny Al▫$_{15}$▫Mn▫$_{3}$▫Be▫$_{2}$▫ and IQC particles into the τ▫$_{1}$▫-Al▫$_{26}$▫Mn▫$_{6}$▫Cu▫$_{4}$▫ phase and precipitation of Al–Mn–Cu precipitates. In the thermomechanically affected zone, new dislocations formed as well as dispersion of the IQC eutectic phase and recrystallisation of the matrix grains. In the heat-affected zone, dissolution of θ’-Al▫$_{2}$▫Cu precipitates occurred. The hardness variation was not severe between the stir and heat-affected zones.

• Jezik: Angleški jezik
• Ključne besede: casting, microstructure, friction stir processing, hardness, transformation, aluminium
• Vrsta gradiva: Članek v reviji
• Tipologija: 1.01 - Izvirni znanstveni članek
• Organizacija: FS - Fakulteta za strojništvo
• Status publikacije: Objavljeno
• Različica publikacije: Objavljena publikacija
• Leto izida: 2022
• Št. strani: 18 str.
• Številčenje: Vol. 12, iss. 5, art. 630
• PID: 20.500.12556/RUL-176308
• UDK: 669.2/.8:620.1
• ISSN pri članku: 2073-4352
• DOI: 10.3390/cryst12050630
• COBISS.SI-ID: 106703363
• Datum objave v RUL: 27.11.2025

Gradivo je del revije

• Naslov: Crystals
• Skrajšan naslov: Crystals
• Založnik: MDPI
• ISSN: 2073-4352
• COBISS.SI-ID: 36677893

Licence

• Licenca: CC BY 4.0, Creative Commons Priznanje avtorstva 4.0 Mednarodna
• Povezava: http://creativecommons.org/licenses/by/4.0/deed.sl
• Opis: To je standardna licenca Creative Commons, ki daje uporabnikom največ možnosti za nadaljnjo uporabo dela, pri čemer morajo navesti avtorja.

Sekundarni jezik

• Jezik: Slovenski jezik
• Ključne besede: litje, mikrostruktura, obdelava s trenjem in mešanjem, trdota, preobrazba, aluminij