Superlubricity of diamond-like carbon coating lubricated with aqueous glycerol under electrified sliding conditions

Kumar, Parveen (avtor), Nadeem, Irfan (avtor), Naseer, Abqaat (avtor), Yaqub, Talha Bin (avtor), Morina, Ardian (avtor), Kalin, Mitjan (avtor)

Hydrogenated diamond-like carbon (H-DLC) coatings are promising materials for minimizing electrical degradation under electrified sliding systems. However, its safe operational voltage threshold required to avoid dielectric breakdown, electrical arcing, and lubrication failure, especially under aqueous lubrication, remains largely unknown. This study explores the sliding performance of steel/H-DLC contact pair lubricated with aqueous glycerol under electrified sliding conditions. The results demonstrate that at applied voltage below 1 V, a stable macroscale superlubricity was observed with a coefficient of friction (COF) ranging between 0.007 and 0.009. The COF increased by 37.5 % when the applied voltage increased to 1.2 V, while a further increase to 1.4 V caused coating degradation, indicating a voltage-induced loss of superlubricity. Analysis revealed that the H-DLC coating retained its structural integrity without graphitization under ≤ 1 V, and the achieved superlubricity was due to the surface passivation by the hydroxyl-terminated groups that form a low shear interface. However, as the applied voltage exceeds the 1 V threshold, sp$^3$-to-sp$^2$ structural transformation occurs, suggesting an electric-field-induced graphitization mechanism that leads to the dielectric breakdown and lubrication failure. These findings provide crucial insights into the electrified sliding performance of H-DLC coatings, rendering them one of the promising candidates for electro-mechanical systems.

• Jezik: Angleški jezik
• Ključne besede: superlubricity, hydrogenated diamond-like carbon, electro-tribology, aqueous glycerol, electrified interfaces, graphitization
• Vrsta gradiva: Članek v reviji
• Tipologija: 1.01 - Izvirni znanstveni članek
• Organizacija: FS - Fakulteta za strojništvo
• Status publikacije: Objavljeno
• Različica publikacije: Objavljena publikacija
• Leto izida: 2026
• Št. strani: 14 str.
• Številčenje: Vol. 215, pt. A, art. 111415
• PID: 20.500.12556/RUL-175994
• UDK: 539.92
• ISSN pri članku: 1879-2464
• DOI: 10.1016/j.triboint.2025.111415
• COBISS.SI-ID: 257496579
• Datum objave v RUL: 17.11.2025

Gradivo je del revije

• Naslov: Tribology international
• Skrajšan naslov: Tribol. int.
• Založnik: Elsevier
• ISSN: 1879-2464
• COBISS.SI-ID: 62108419

Licence

• Licenca: CC BY 4.0, Creative Commons Priznanje avtorstva 4.0 Mednarodna
• Povezava: http://creativecommons.org/licenses/by/4.0/deed.sl
• Opis: To je standardna licenca Creative Commons, ki daje uporabnikom največ možnosti za nadaljnjo uporabo dela, pri čemer morajo navesti avtorja.

Sekundarni jezik

• Jezik: Slovenski jezik
• Ključne besede: supermazljivost, hidrogeniran diamantu podoben ogljik, elektrotribologija, vodni glicerol, elektrificirani vmesniki, grafitizacija