Effects of beech wood surface treatment with polyethylenimine solution prior to finishing with water-based coating
ID Palija, Tanja (Avtor), ID Rančić, Milica (Avtor), ID Djikanović, Daniela (Avtor), ID Radotić, Ksenija (Avtor), ID Petrič, Marko (Avtor), ID Pavlič, Matjaž (Avtor), ID Jaić, Milan (Avtor)

.pdfPDF - Predstavitvena datoteka, prenos (10,14 MB)
MD5: 0E8F8287CB622653A41B19EEB2A83DED
URLURL - Izvorni URL, za dostop obiščite https://www.mdpi.com/2073-4360/17/1/77 Povezava se odpre v novem oknu

Izvleček
The surfaces of beech wood samples were treated with polyethylenimine (PEI) solutions at three different concentrations—0.5%, 1% and 2%—and two molecular weights—low molecular weight (LMW) and high molecular weight (HMW). The effects of PEI surface treatment of wood were characterized by FT-IR spectroscopy, the penetration depth of PEI (EPI fluorescence spectroscopy), the bonding position of PEI (by SEM), the wetting and surface energy, and the water uptake. After PEI treatment, the samples were coated with a water-based transparent acrylic coating (WTAC). The dry film thickness, the penetration depth of the coating, the adhesion strength and the surface roughness of the coated wood surface were evaluated. EPI fluorescence and SEM micrographs showed that PEI HMW chains were deposited on the surface, in contrast to PEI LMW, which penetrates deeper into layers of the wood cells. Treatment with a 1% PEI HMW solution resulted in a 72% reduction in water uptake of the wood (compared to untreated samples after 5 min of applying water droplets to the surface) and a 23.2% reduction in surface energy (compared to untreated samples) while maintaining the adhesion strength of the applied WTAC. The lower water uptake of the treated wood samples reduced the roughness of the coated surface, which is particularly important when the wood surface is finished with water-based coatings.

Jezik:Angleški jezik
Ključne besede:les, polyelectrolyte, polyethyleneimine, water-based coating, wood surface finishing
Vrsta gradiva:Članek v reviji
Tipologija:1.01 - Izvirni znanstveni članek
Organizacija:BF - Biotehniška fakulteta
Status publikacije:Objavljeno
Različica publikacije:Objavljena publikacija
Leto izida:2025
Št. strani:Str. 1-23
Številčenje:Vol. 17, iss. 1, [article no.] 77
PID:20.500.12556/RUL-166310 Povezava se odpre v novem oknu
UDK:630*8
ISSN pri članku:2073-4360
DOI:10.3390/polym17010077 Povezava se odpre v novem oknu
COBISS.SI-ID:221148675 Povezava se odpre v novem oknu
Datum objave v RUL:07.01.2025
Število ogledov:98
Število prenosov:17
Metapodatki:XML DC-XML DC-RDF
:
Kopiraj citat
Objavi na:Bookmark and Share

Gradivo je del revije

Naslov:Polymers
Skrajšan naslov:Polymers
Založnik:MDPI
ISSN:2073-4360
COBISS.SI-ID:517951257 Povezava se odpre v novem oknu

Sekundarni jezik

Jezik:Slovenski jezik
Ključne besede:les, polielektrolit, polietileneimi, vodni premaz, površinska obdelava lesa

Podobna dela

Podobna dela v RUL:
Podobna dela v drugih slovenskih zbirkah:

Nazaj