Degradation processes of two compound layers on nitrided surfaces during the wear test by ‘‘block on hot Al cylinder’’

Lamut, Martin (avtor), Burja, Jaka (avtor), Terčelj, Milan (avtor), Kugler, Goran (avtor), Bombač, David (avtor)

The results obtained in the study help to explain the degradation process of the nitrided steel compound layer. Compound layers with different properties on gas-nitrided H10 tool steel blocks were tested for wear with ‘‘block on hot Al cylinder’’. Degradation processes were observed on both compound layers with different properties and at three contact pressures. In order to observe the degradation processes in the compound layers, the wear tests were interrupted at various fixed time intervals and the resulting changes were closely monitored. The comprehensive analysis highlighted the complexity of the degradation process in the compound layers and emphasized the existence of complex relationships between the above-mentioned parameters. The reaction of the nitrided steel surface with hot Al is more pronounced in areas with lower contact pressure, while adhesive removal and furrow formation are pronounced in areas with low and medium contact pressure. This process begins with a sufficient density of the areas where islands of adhesive removal are located, their enlargement during the test, the breaking up of the walls between them, and finally the removal of the compound layer in the sliding direction, which appears as furrowing in the final phase of wear.

• Jezik: Angleški jezik
• Ključne besede: wear, nitrided steel, hot-work tool steel, thermal fatigue, aluminium extrusion, tool surface degradation
• Vrsta gradiva: Članek v reviji
• Tipologija: 1.01 - Izvirni znanstveni članek
• Organizacija: NTF - Naravoslovnotehniška fakulteta
• Status publikacije: Objavljeno
• Različica publikacije: Objavljena publikacija
• Leto izida: 2024
• Št. strani: Str. 4006–4027
• Številčenje: Vol. 76, no. 8
• PID: 20.500.12556/RUL-159822
• UDK: 669
• ISSN pri članku: 1047-4838
• DOI: 10.1007/s11837-024-06693-1
• COBISS.SI-ID: 200251907
• Datum objave v RUL: 26.07.2024

LAMUT, Martin, BURJA, Jaka, TERČELJ, Milan, KUGLER, Goran in BOMBAČ, David, 2024, Degradation processes of two compound layers on nitrided surfaces during the wear test by ‘‘block on hot Al cylinder’’. JOM : the journal of The Minerals, Metals & Materials Society (TMS) [na spletu]. 2024. Vol. 76, no. 8. [Dostopano 3 april 2025]. DOI 10.1007/s11837-024-06693-1. Pridobljeno s: https://repozitorij.uni-lj.si/IzpisGradiva.php?lang=slv&id=159822

Gradivo je del revije

• Naslov: JOM : the journal of The Minerals, Metals & Materials Society (TMS)
• Skrajšan naslov: JOM
• Založnik: Springer Nature, The Minerals, Metals & Materials Society
• ISSN: 1047-4838
• COBISS.SI-ID: 6745605

Licence

• Licenca: CC BY 4.0, Creative Commons Priznanje avtorstva 4.0 Mednarodna
• Povezava: http://creativecommons.org/licenses/by/4.0/deed.sl
• Opis: To je standardna licenca Creative Commons, ki daje uporabnikom največ možnosti za nadaljnjo uporabo dela, pri čemer morajo navesti avtorja.

Sekundarni jezik

• Jezik: Slovenski jezik
• Ključne besede: obraba, nitrirano jeklo, orodno jeklo za delo v vročem, toplotno utrujanje, ekstruzija aluminija, obraba površine orodja