The effects of microcrystalline cellulose addition on the properties of wood–PLA filaments for 3D printing

Krapež, Daša (avtor), Schöflinger, Manfred (avtor), Leßlhumer, Jürgen (avtor), Gradišar Centa, Urška (avtor), Žigon, Jure (avtor), Kariž, Mirko (avtor)

This paper describes the use of microcrystalline cellulose (MCC) as an additive in wood-polylactic acid (PLA) filaments suitable for 3D printing. Filaments prepared with PLA, thermally modified (TM) wood, and three different MCC loadings (1, 3, and 5 wt%) by two-step melt blending in the extruder were characterized with respect to their rheological, thermal, and mechanical response. The analyses demonstrate that a low MCC content (1%) improves the mobility of the polymer chains and contributes to a higher elasticity of the matrix chain, a higher crystallinity, a lower glass transition temperature (by 1.66 °C), and a lower melting temperature (by 1.31 °C) and leads to a higher tensile strength (1.2%) and a higher modulus of elasticity (12.1%). Higher MCC loading hinders the mobility of the polymer matrix and leads to a rearrangement of the crystal lattice structure, resulting in a decrease in crystallinity. Scanning electron micrographs show that the cellulose is well distributed and dispersed in the PLA matrix, with some agglomeration occurring at higher MCC levels. The main objective of this study was to develop and evaluate a filament containing an optimal amount of MCC to improve compatibility between wood and PLA, optimize melt processability, and improve mechanical properties. It can be concluded that a 1% addition of MCC favorably changes the properties of the wood–PLA filaments, while a higher MCC content does not have this effect.

• Jezik: Angleški jezik
• Ključne besede: microcrystalline cellulose, thermally modified wood, wood–plastic filaments, rheological properties
• Vrsta gradiva: Članek v reviji
• Tipologija: 1.01 - Izvirni znanstveni članek
• Organizacija: BF - Biotehniška fakulteta ; FS - Fakulteta za strojništvo
• Status publikacije: Objavljeno
• Različica publikacije: Objavljena publikacija
• Leto izida: 2024
• Št. strani: 20 str.
• Številčenje: Vol. 16, iss. 6, art. 836
• PID: 20.500.12556/RUL-155071
• UDK: 630*8
• ISSN pri članku: 2073-4360
• DOI: 10.3390/polym16060836
• COBISS.SI-ID: 189394691
• Datum objave v RUL: 19.03.2024

Gradivo je del revije

• Naslov: Polymers
• Skrajšan naslov: Polymers
• Založnik: MDPI
• ISSN: 2073-4360
• COBISS.SI-ID: 517951257

Licence

• Licenca: CC BY 4.0, Creative Commons Priznanje avtorstva 4.0 Mednarodna
• Povezava: http://creativecommons.org/licenses/by/4.0/deed.sl
• Opis: To je standardna licenca Creative Commons, ki daje uporabnikom največ možnosti za nadaljnjo uporabo dela, pri čemer morajo navesti avtorja.

Sekundarni jezik

• Jezik: Slovenski jezik
• Ključne besede: mikrokristalinična celuloza, termično modificiran les, lesno-plastični filamenti, reološke lastnosti