In-depth comparison of an industrially extruded powder and ingot Al alloys

Bombač, David (avtor), Cvahte, Peter (avtor), Balog, Martin (avtor), Kugler, Goran (avtor), Terčelj, Milan (avtor)

An industrial press was used to consolidate compacted aluminum powder with a nominal diameter in the range of 1 µm. Direct and indirect hot-extrusion processes were used, and suitable process parameters were determined from heating conditions, ram speeds and billet temperatures. For comparison, a direct-extrusion press for hot extrusion of a conventional aluminum alloy AA 1050 was used. The extruded Al powder showed better mechanical properties and showed a thermal stability of the mechanical properties after annealing treatments. To increase the theoretical density of the directly extruded Al powder, single-hit hot-compression tests were carried out. Activation energies for hot forming were calculated from hot-compression tests carried out in the temperature range 300–580 °C, at different strain rates. Processing maps were used to demonstrate safe hot-working conditions, to obtain an optimal microstructure after hot forming of extruded Al powder.

• Jezik: Angleški jezik
• Ključne besede: aluminum powder, hot extrusion, hot compression, activation energy
• Vrsta gradiva: Članek v reviji
• Tipologija: 1.01 - Izvirni znanstveni članek
• Organizacija: NTF - Naravoslovnotehniška fakulteta
• Status publikacije: Objavljeno
• Različica publikacije: Objavljena publikacija
• Leto izida: 2020
• Št. strani: 18 str.
• Številčenje: Vol. 10, iss. 11, art. 1483
• PID: 20.500.12556/RUL-134460
• UDK: 669
• ISSN pri članku: 2075-4701
• DOI: 10.3390/met10111483
• COBISS.SI-ID: 36233219
• Datum objave v RUL: 17.01.2022

Gradivo je del revije

• Naslov: Metals
• Skrajšan naslov: Metals
• Založnik: MDPI AG
• ISSN: 2075-4701
• COBISS.SI-ID: 15976214

Licence

• Licenca: CC BY 4.0, Creative Commons Priznanje avtorstva 4.0 Mednarodna
• Povezava: http://creativecommons.org/licenses/by/4.0/deed.sl
• Opis: To je standardna licenca Creative Commons, ki daje uporabnikom največ možnosti za nadaljnjo uporabo dela, pri čemer morajo navesti avtorja.
• Začetek licenciranja: 06.11.2020