Particleboards with partially liquefied bark of different particle sizes
ID Jiang, Wen (Avtor), ID Adamopoulos, Stergios (Avtor), ID Petrič, Marko (Avtor), ID Šernek, Milan (Avtor), ID Medved, Sergej (Avtor)

.pdfPDF - Predstavitvena datoteka, prenos (754,53 KB)
MD5: A822E481DB9582573593061FF214DEA3

Izvleček
This paper presents a novel method of partially liquefying bark sawmilling waste for use in making particleboards. Maritime pine (Pinus pinaster Ait.) bark of different particle sizes (fine, medium, coarse, and mixed) was partially liquefied in the presence of ethylene glycol as a solvent and sulphuric acid as a catalyst at 180°C for 30 minutes. Single-layer particleboards were prepared by mixing partially liquefied bark (PLB) and wood chips at a ratio of 0.25 with no adhesives (group A) and at ratios of 0.25 or 0.1 with melamine-urea-formaldehyde (MUF) adhesives for additional bonding (groups B and C respectively). Mechanical and physical properties of the particleboards were tested according to European standards. The results showed that the boards in group A had lower densities, inferior mechanical properties and higher moisture content than those in groups B and C. Bark particle size had a significant effect on the mechanical properties of particleboards within each group. Additional MUF bonding and avoidance of coarse bark particles had a positive effect on mechanical properties. The thickness swelling (TS) and water absorption (WA) values of MUF-bonded boards were lower than those of boards without MUF, and greater addition of PLB produced particleboards with better water resistance. Bark particle size was not as critical for TS and WA as for mechanical properties. The overall results suggested using a bark particle size of < 2 mm for further studies.

Jezik:Angleški jezik
Ključne besede:skorja, etilen glikol, utekočinjenje, MUF lepilo, vlaknene plošče, Pinus pinaster Ait.
Tipologija:1.01 - Izvirni znanstveni članek
Organizacija:BF - Biotehniška fakulteta
Leto izida:2021
Status objave pri reviji:Objavljeno
Verzija članka:Založnikova različica članka
Št. strani:Str. 43-57
Številčenje:Vol. 64, no. 207
PID:20.500.12556/RUL-128904 Povezava se odpre v novem oknu
UDK:630*8
ISSN pri članku:1644-3985
DOI:10.12841/wood.1644-3985.363.10 Povezava se odpre v novem oknu
COBISS.SI-ID:70741507 Povezava se odpre v novem oknu
Datum objave v RUL:13.08.2021
Število ogledov:375
Število prenosov:30
Metapodatki:XML RDF-CHPDL DC-XML DC-RDF
:
Kopiraj citat
Objavi na:AddThis
AddThis uporablja piškotke, za katere potrebujemo vaše privoljenje.
Uredi privoljenje...

Gradivo je del revije

Naslov:Drewno
Založnik:Wydawnictwo Instytutu Technologii Drewna
ISSN:1644-3985
COBISS.SI-ID:1255590 Povezava se odpre v novem oknu

Sekundarni jezik

Jezik:Angleški jezik
Ključne besede:bark, ethylene glycol, liquefaction, maritime pine, MUF resin, particleboard

Podobna dela

Podobna dela v RUL:
Podobna dela v drugih slovenskih zbirkah:

Nazaj