The dynamics of thickness swelling and bond strength loss of different wood-based panels at exposure to humid climate and immersion into water
Medved, Sergej (Avtor), Žgajner, Damjan (Avtor), Antonović, Alan (Avtor)

URLURL - Izvorni URL, za dostop obiščite http://www.les-wood.si/index.php/leswood/article/view/64/41 Povezava se odpre v novem oknu
.pdfPDF - Predstavitvena datoteka, prenos (1,12 MB)
MD5: C179DE6B3F3C7138DEF57EF14D77D83E

Izvleček
An important aspect of wood-based panel usability, especially for construction, load bearing purposes or when in use for longer time, is its resistance against water. The resistance against water is related to type of wood-based panel, morphological characteristics of the constituents that panel is made of, and from the resin that was used for bonding. In an experiment we used four different wood-based panels, namely MDF (urea-formaldehyde adhesive), particleboard (urea-formaldehyde adhesive), OSB (melamine-urea-formaldehyde adhesive) and beech plywood (melamine-urea-formaldehyde adhesive). All panels were immersed into water and exposed to a humid climate for 90 days. Thickness swelling, compression shear strength and shear strength were determined after 1, 5, 30 and 90 days. The results showed that the highest strength decrease was observed at immersion into water. The lowest compression shear strength after immersion into water and exposure to a humid climate was determined for MDF. The occurrence of constituent failure due to mexposure to water was demonstrated through SEM analysis.

Jezik:Angleški jezik
Ključne besede:plywood, OSB, particleboard, MDF, compression shear strength, shear strength, water, humid condition
Vrsta gradiva:Članek v reviji (dk_c)
Tipologija:1.01 - Izvirni znanstveni članek
Organizacija:BF - Biotehniška fakulteta
Leto izida:2019
Št. strani:Str. 25-35
Številčenje:Letn. 68, št. 1
UDK:630*862.9
ISSN pri članku:0024-1067
COBISS.SI-ID:3085449 Povezava se odpre v novem oknu
Število ogledov:122
Število prenosov:59
Metapodatki:XML RDF-CHPDL DC-XML DC-RDF
 
Skupna ocena:(0 glasov)
Vaša ocena:Ocenjevanje je dovoljeno samo prijavljenim uporabnikom.
:
Objavi na:AddThis
AddThis uporablja piškotke, za katere potrebujemo vaše privoljenje.
Uredi privoljenje...

Gradivo je del revije

Naslov:Les
Skrajšan naslov:Les
Založnik:Zveza društev inženirjev in tehnikov gozdarstva in lesarstva Slovenije, Zveza društev inženirjev in tehnikov gozdarstva in lesarstva Slovenije, Biotehniška fakulteta, Oddelek za lesarstvo
ISSN:0024-1067
COBISS.SI-ID:13940224 Povezava se odpre v novem oknu

Gradivo je financirano iz projekta

Financer:ARRS - Agencija za raziskovalno dejavnost Republike Slovenije (ARRS)
Številka projekta:P4-0015
Naslov:Les in lignocelulozni kompoziti

Financer:ARRS - Agencija za raziskovalno dejavnost Republike Slovenije (ARRS)
Številka projekta:L4-7547
Naslov:Obnašanje lesa in lignoceluloznih kompozitov v zunanjih pogojih

Licence

Licenca:CC BY 4.0, Creative Commons Priznanje avtorstva 4.0 Mednarodna
Povezava:http://creativecommons.org/licenses/by/4.0/deed.sl
Opis:To je standardna licenca Creative Commons, ki daje uporabnikom največ možnosti za nadaljnjo uporabo dela, pri čemer morajo navesti avtorja.
Začetek licenciranja:29.04.2021

Sekundarni jezik

Jezik:Slovenski jezik
Naslov:Dinamika spreminjanja debelinskega nabreka in kakovosti zlepljenosti različnih lesnih ploščnih kompozitov pri vlažni klimi in potopitvi v vodo
Izvleček:
Pomemben dejavnik uporabnosti lesnih ploščnih kompozitov pri gradnji in nosilnih konstrukcijah je odpornost le-teh proti delovanju vode. Odpornost proti delovanju vode je odvisna od vrste lesnega ploščnega kompozita, morfoloških lastnosti gradnika, iz katerega je plošča narejena, in lepila, uporabljenega za lepljenje. Za izvedbo raziskave smo uporabili štiri različne lesne ploščne kompozite in sicer MDF (urea-formaldehidno lepilo), iverno ploščo (urea-formaldehidno lepilo), OSB (melamin-urea-formaldehidno lepilo) in bukovo furnirno ploščo (melamin-urea-formalde-hidno lepilo). Vse plošče so bile potopljene v vodo in izpostavljene vlažnim klimatskim pogojem. Določili smo debelinski nabrek, tlačni strig in strižno trdnost. Lastnosti so bile določene 1, 5, 30 in 90 dni po izpostavitvi. Največja sprememba trdnosti je bila ugotovljena pri preskušancih, potopljenih v vodo. Najnižja odpornost proti delovanju vode je bila ugotovljena pri MDF plošči. S SEM slikovno analizo smo prikazali nastanek razpok in porušitve zgradbe gradnikov. Ključne besede: furnirna plošča, OSB, iverna plošča, MDF, tlačni strig, strižna trdnost, voda, vlažna klima.

Ključne besede:furnirna plošča, OSB, iverna plošča, MDF, tlačni strig, strižna trdnost, voda, vlažna klima

Podobna dela

Podobna dela v RUL:
Podobna dela v drugih slovenskih zbirkah:

Komentarji

Dodaj komentar

Za komentiranje se morate prijaviti.

Komentarji (0)
0 - 0 / 0
 
Ni komentarjev!

Nazaj