Izdelava kompozitnega izdelka s 3D tiskanjem in vakuumsko infuzijo
Bešić, Edo (Avtor), Valentinčič, Joško (Mentor) Več o mentorju... Povezava se odpre v novem oknu, Šturm, Roman (Komentor)

.pdfPDF - Predstavitvena datoteka, prenos (5,70 MB)
MD5: 011ECE709019E539078ACA1DE345880B

Izvleček
Aditivne tehnologije, imenovane tudi tehnologije 3D tiskanja, omogočajo hitro izdelavo precej kompleksnih oblik izdelkov iz polimerov, gume in tudi kovin. Vakuumska infuzija je postopek izdelave kompozitov, kjer s pomočjo podtlaka prepojimo ojačitvena vlakna s tekočim duroplastom. Preizkusili smo vpliv dodane epoksi smole na mehanske lastnosti poroznih preizkušancev iz PLA in LayFomm 60, izdelanih z metodo ciljnega nalaganja. Preizkušance smo primerjali z referenčnimi preizkušanci iz PLA s 50 in 100-% zapolnitvijo. Mehanske lastnosti smo testirali s Charpyjevim preizkusom udarne žilavosti in s tritočkovnim upogibnim preizkusom. Kompozitni preizkušanci iz epoksi smole in PLA so imeli višjo trdnost od preizkušancev iz PLA s 50-% zapolnitvijo; njihova trdnost je bila na ravni PLA s 100-% zapolnitvijo. Charpyjev preizkus je pokazal, da se kompozitni material uvrsti med PLA s 100-% zapolnitvijo, ki je bolj žilav, in PLA s 50-% zapolnitvijo, ki ima manjšo žilavost. Impregnacija preizkušancev iz LayFomm 60 z epoksi smolo je bila slaba, zato so slabe tudi mehanske lastnosti takega kompozita.

Jezik:Slovenski jezik
Ključne besede:aditivne tehnologije 3D tiskanje metoda ciljnega nalaganja kompozit PLA epoksi vakuumska infuzija mehanske lastnosti udarna žilavost upogibna trdnost
Vrsta gradiva:Magistrsko delo/naloga (mb22)
Organizacija:FS - Fakulteta za strojništvo
Leto izida:2018
Število ogledov:657
Število prenosov:330
Metapodatki:XML RDF-CHPDL DC-XML DC-RDF
 
Skupna ocena:(0 glasov)
Vaša ocena:Ocenjevanje je dovoljeno samo prijavljenim uporabnikom.
:
Objavi na:AddThis
AddThis uporablja piškotke, za katere potrebujemo vaše privoljenje.
Uredi privoljenje...

Sekundarni jezik

Jezik:Angleški jezik
Naslov:Composite Material Manufacturing by 3D Printing and Vacuum Resin Infusion
Izvleček:
Additive manufacturing technologies, also known as 3D printing technologies, are used to quickly create objects with complicated shapes. Vacuum infusion is a technology used in the creation of composite materials that creates underpressure in the object in order to draw the liquid thermoset in it. In this work the viability of combining the two technologies to create composite test specimens from PLA or LayFomm 60 made by Fused Deposition Modelling (FDM) technology and reinforced with epoxy resin that is applied with the process of vacuum infusion is explored. Mechanical properties of the materials were tested with Charpy impact test and with three-point bend test. Results were compared with the reference test specimens made from PLA with 50% and 100% infill densities. Composite material made from PLA and epoxy resin had higher tensile strength in three-point bemd test than PLA with 50% infll density and was on par with PLA with 100% infill density. Charpy test has shown the composite material has impact strength that is lower than the one from PLA with 100% infill density and higher than PLA with 50% infill density. Tensile strength of specimens made from LayFomm 60 and epoxy resin was low due to the bad impregnation of the material with epoxy resin.

Ključne besede:additive technologies fused deposition modelling 3D printing composite PLA epoxy vacuum resin infusion mechanical properties impact strength tensile strength

Podobna dela

Podobna dela v RUL:
Podobna dela v drugih slovenskih zbirkah:

Komentarji

Dodaj komentar

Za komentiranje se morate prijaviti.

Komentarji (0)
0 - 0 / 0
 
Ni komentarjev!

Nazaj