Mechanical properties of 3D-printed and milled composite resins for definitive restorations : an in vitro comparison of initial strength and fatigue behavior

Prause, Elisabeth (avtor), Malgaj, Tine (avtor), Kocjan, Andraž (avtor), Beuer, Florian (avtor), Hey, Jeremias (avtor), Jevnikar, Peter (avtor), Schmidt, Franziska (avtor)

Objective: To evaluate the flexural strength and fatigue behavior of a novel 3D-printed composite resin for definitive restorations. Materials and Methods: Fifty disc-shaped specimens were manufactured from each of a nanohybrid composite resin (NHC), polymer-infiltrated ceramic network (PICN), and 3D-printed composite resin (3D) with CAD-CAM technology. Biaxial flexural strength (σ$_{in}$) (n = 30 per group) and biaxial flexural fatigue strength (σ$_{ff}$) (n = 20 per group) were measured using piston-on-three-balls method, employing a staircase approach of 105 cycles. Weibull statistics, relative-strength degradation calculations, and fractography were performed. The results were analyzed with 1-way ANOVA and Games-Howell post hoc test (α = 0.05). Results: Significant differences in σ$_{in}$ and σ$_{ff}$ among the groups (p < 0.001) were detected. The NHC group provided the highest mean ± standard deviation σ$_{in}$ and σ$_{ff}$ (237.3 ± 31.6 MPa and 141.3 ± 3.8 MPa), followed by the PICN (140.3 ± 12.9 MPa and 73.5 ± 9.9 MPa) and the 3D (83.6 ± 18.5 MPa and 37.4 ± 23.8 MPa) groups. The 3D group exhibited significantly lower Weibull modulus (m = 4.7) and up to 15% higher relative strength degradation with areas of nonhomogeneous microstructure as possible fracture origins. Conclusions: The 3D-printed composite resin exhibited the lowest mechanical properties, where areas of nonhomogeneous microstructure developed during the mixing procedure served as potential fracture origins.

• Jezik: Angleški jezik
• Ključne besede: 3D-printed composite resins, Weibull, additive manufacturing, flexural fatigue strength, flexural strength, milled composite resins, staircase approach
• Vrsta gradiva: Članek v reviji
• Tipologija: 1.01 - Izvirni znanstveni članek
• Organizacija: MF - Medicinska fakulteta
• Status publikacije: Objavljeno
• Različica publikacije: Objavljena publikacija
• Leto izida: 2024
• Št. strani: Str. 391–401
• Številčenje: Vol. 36, iss. 2
• PID: 20.500.12556/RUL-154085
• UDK: 616.31
• ISSN pri članku: 1708-8240
• DOI: 10.1111/jerd.13132
• COBISS.SI-ID: 163917571
• Datum objave v RUL: 24.01.2024

PRAUSE, Elisabeth, MALGAJ, Tine, KOCJAN, Andraž, BEUER, Florian, HEY, Jeremias, JEVNIKAR, Peter in SCHMIDT, Franziska, 2024, Mechanical properties of 3D-printed and milled composite resins for definitive restorations : an in vitro comparison of initial strength and fatigue behavior. Journal of esthetic and restorative dentistry [na spletu]. 2024. Vol. 36, no. 2. [Dostopano 30 april 2025]. DOI 10.1111/jerd.13132. Pridobljeno s: https://repozitorij.uni-lj.si/IzpisGradiva.php?lang=slv&id=154085

Gradivo je del revije

• Naslov: Journal of esthetic and restorative dentistry
• Založnik: Wiley
• ISSN: 1708-8240
• COBISS.SI-ID: 3185684

Licence

• Licenca: CC BY-NC-ND 4.0, Creative Commons Priznanje avtorstva-Nekomercialno-Brez predelav 4.0 Mednarodna
• Povezava: http://creativecommons.org/licenses/by-nc-nd/4.0/deed.sl
• Opis: Najbolj omejujoča licenca Creative Commons. Uporabniki lahko prenesejo in delijo delo v nekomercialne namene in ga ne smejo uporabiti za nobene druge namene.

Sekundarni jezik

• Jezik: Slovenski jezik
• Ključne besede: 3D-natisnjene kompozitne smole, aditivna izdelava, upogibna napetost, mlete kompozitne smole

Projekti

• Financer: ARRS - Agencija za raziskovalno dejavnost Republike Slovenije
• Številka projekta: P2-0087
• Naslov: Keramični in komplementarni materiali za napredne inženirske in biomedicinske aplikacije

• Financer: ARRS - Agencija za raziskovalno dejavnost Republike Slovenije
• Številka projekta: J3-3064
• Naslov: Predklinične in klinične raziskave cirkonijeve oksidne dentalne keramike, izdelane s tehnologijami aditivnega oblikovanja (ZIRAMDENT)