Trdan, Uroš (avtor), Tomokazu, Sano (avtor), Klobčar, Damjan (avtor), Sano, Yuji (avtor), Grum, Janez (avtor), Šturm, Roman (avtor)

This work reports for the first time the effect of femtosecond laser shock peening (fLSP) without a sacrificial overlay under atmospheric conditions (no confinement) on the corrosion behaviour of AA2024-T3. After fLSP and additional exposure to air a superhydrophobic state (θ=160 ± 4°) is achieved. Moreover, fLSPed corrosion-resistant surface contributes to increased polarization resistance, reduced corrosion current and lower anodic dissolution, with long-term stability in aggressive chloride solution. Furthermore, SEM/EDS characterisation reveals reduction in pitting and complete eradication of intergranular corrosion (IGC) attack due to reduced metal/electrolyte contact area and homogeneous, refined microstructure which prevents chain-link IGC propagation.

• Jezik: Angleški jezik
• Ključne besede: aluminium, aluminium alloy 2024-T3, polarization, scanning electron microscope - SEM, intergranular corrosion, pitting corrosion
• Vrsta gradiva: Članek v reviji
• Tipologija: 1.01 - Izvirni znanstveni članek
• Organizacija: FS - Fakulteta za strojništvo
• Status publikacije: Objavljeno
• Različica publikacije: Recenzirani rokopis
• Poslano v recenzijo: 17.04.2018
• Datum sprejetja članka: 07.08.2018
• Datum objave: 14.08.2018
• Leto izida: 2018
• Št. strani: Str. 46-55
• Številčenje: Vol. 143
• PID: 20.500.12556/RUL-127264
• UDK: 620.1(045)
• ISSN pri članku: 0010-938X
• DOI: 10.1016/j.corsci.2018.08.030
• COBISS.SI-ID: 16218651
• Datum objave v RUL: 01.06.2021

TRDAN, Uroš, TOMOKAZU, Sano, KLOBČAR, Damjan, SANO, Yuji, GRUM, Janez in ŠTURM, Roman, 2018, Improvement of corrosion resistance of AA2024-T3 using femtosecond laser peening without protective and confining medium. Corrosion science [na spletu]. 2018. Vol. 143, p. 46–55. [Dostopano 2 april 2025]. DOI 10.1016/j.corsci.2018.08.030. Pridobljeno s: https://repozitorij.uni-lj.si/IzpisGradiva.php?lang=slv&id=127264

Gradivo je del revije

• Naslov: Corrosion science
• Skrajšan naslov: Corros. sci.
• Založnik: Pergamon Press
• ISSN: 0010-938X
• COBISS.SI-ID: 5881607

Licence

• Licenca: CC BY-NC 4.0, Creative Commons Priznanje avtorstva-Nekomercialno 4.0 Mednarodna
• Povezava: http://creativecommons.org/licenses/by-nc/4.0/deed.sl
• Opis: Licenca Creative Commons, ki prepoveduje komercialno uporabo, vendar uporabniki ne rabijo upravljati materialnih avtorskih pravic na izpeljanih delih z enako licenco.
• Začetek licenciranja: 01.10.2018

Sekundarni jezik

• Jezik: Slovenski jezik
• Ključne besede: aluminij, aluminijeva zlitina 2024-T3, polarizacija, vrstični elektronski mikroskop - SEM, interkristalna korozija, jamičasta korozija