Vpliv deformacije in toplotne obdelave na mehanske lastnosti aluminijeve zlitine EN AW-5754
ID Mlinar, Timotej (Avtor), ID Fajfar, Peter (Mentor) Več o mentorju... Povezava se odpre v novem oknu, ID Cvahte, Peter (Komentor)

.pdfPDF - Predstavitvena datoteka, prenos (2,99 MB)
MD5: 38A8C2B956BB9D751FAF344C4E4B2966

Izvleček
Aluminij-magnezijeve zlitine so zaradi svoje dobre korozijske obstojnosti in dokaj visokih trdnostnih lastnosti dobro zastopane v transportni industriji. Le-ta teži k izdelavi varčnejših in okolju prijaznejših prevoznih sredstev z dovolj visokimi mehanskimi lastnostmi. V diplomskem delu smo obravnavali vpliv deformacije in toplotne obdelave na mehanske lastnosti aluminijeve zlitine EN AW 5754. Vhodna surovina je bila toplo valjana pločevina (vzorec 1) debeline 5 mm, katera je z 212 MPa kazala najnižjo vrednost natezne trdnosti. Nadalje je bila pločevina še hladno valjana v treh prehodih in vsak prehod je bil posebej obravnavan. Pločevina zadnjega prehoda (vzorec 4) debeline 2 mm je kazala najvišjo natezno trdnost z vrednostjo 319 MPa, vendar je njen raztezek ob porušitvi znašal zgolj 5,7 %, napram vzorcu 1, kjer je raztezek ob porušitvi dosegel vrednost 27,5 %. Eksponent deformacijskega utrjevanja se pri kovinah po navadi giblje od 0,1 do 0,5 in kaže sposobnost preoblikovanja materiala. Vzorec 1 ima najboljšo preoblikovalnost z vrednostjo eksponenta deformacijskega utrjevanja 0,2984. Le-ta med hladnim valjanjem postopoma pada in pri vzorcu 4 doseže vrednost 0,0764. Toplotna obdelava vzorcev je potekala v temperaturnem območju od 240 °C do 300 °C pri časih 60 min, 240 min in 480 min. Med toplotno obdelavo so se vrednosti mehanskih lastnosti hladno valjanih vzorcev približevale vrednostim toplo valjane pločevine.

Jezik:Slovenski jezik
Ključne besede:aluminijeva zlitina, deformacija, toplotna obdelava, natezni preizkus, mehanske lastnosti
Vrsta gradiva:Diplomsko delo/naloga
Organizacija:NTF - Naravoslovnotehniška fakulteta
Leto izida:2020
PID:20.500.12556/RUL-120956 Povezava se odpre v novem oknu
COBISS.SI-ID:31469059 Povezava se odpre v novem oknu
Datum objave v RUL:28.09.2020
Število ogledov:3053
Število prenosov:386
Metapodatki:XML DC-XML DC-RDF
:
MLINAR, Timotej, 2020, Vpliv deformacije in toplotne obdelave na mehanske lastnosti aluminijeve zlitine EN AW-5754 [na spletu]. Diplomsko delo. [Dostopano 13 julij 2025]. Pridobljeno s: https://repozitorij.uni-lj.si/IzpisGradiva.php?lang=slv&id=120956
Kopiraj citat
Objavi na:Bookmark and Share

Sekundarni jezik

Jezik:Angleški jezik
Naslov:Effect of deformation and heat treatment on the mechanical properties of aluminium alloy EN AW-5754
Izvleček:
Aluminum-magnesium alloys are well represented in the transport industry due to their good corrosion resistance and relatively high strength properties. The transport industry strives to produce more economical and environmentally friendly means of transport with sufficiently high mechanical properties. In the diploma work we investigated the influence of deformation and heat treatment on the mechanical properties of aluminum alloy EN AW 5754. The input raw material was hot rolled sheet metal (sample 1) 5 mm thick, which showed the lowest value of tensile strength with 212 MPa. Furthermore, the sheet was cold rolled in three passes and each pass was treated separately. Cold rolled sheet metal (sample 4) 2 mm thick showed the highest tensile strength with a value of 319 MPa, but its elongation at break was only 5.7 %, compared to sample 1, where the elongation at break reached 27.5 %. The strain hardening exponent for metals usually ranges from 0.1 to 0.5 and shows the ability to transform the material. Sample 1 has the best deformability with a value of the strain hardening exponent of 0.2984, which gradually decreases during cold rolling and reaches a value of 0.0764 in sample 4. The heat treatment of the samples took place in the temperature range from 240 °C to 300 °C at times of 60 min, 240 min and 480 min. During the heat treatment, the values of the mechanical properties of the cold-rolled samples approached the values of the hot-rolled sheet.

Ključne besede:aluminium alloy, deformation, heat treatment, tensile test, mechanical properties

Podobna dela

Podobna dela v RUL:
  1. Quantification of selected novel inhibitors of butylcholinesterase in brain tissue and blood plasma of a rat
  2. Development of a rat blood plasma and brain tissue sample preparation procedure for the quantification of novel cholinestease inhibitors
  3. Mechanisms of vesiculation and stability of vesicular structures in samples of human blood plasma and marine microalgae
  4. Viscosity of plasma as a key factor in assessment of extracellular vesicles by light scattering
  5. Identification of Aggregatibacter acinomycetemcomitans RNA binding proteins
Podobna dela v drugih slovenskih zbirkah:
  1. Separation of porcine blood and electrophoresis proteins in porcine blood plasma
  2. Structural and functional determinants of TDP-43 aggregation
  3. Measurement of prostanoids in human blood plasma with the use of gas cromatography and mass spectrometry
  4. Rapid and sensitive determination of ChE activity in blood plasma

Nazaj