Karakterizacija zlitine AlSi7Mg0,3 : diplomsko delo
ID Sovinc, Martina (Author), ID Markoli, Boštjan (Mentor) More about this mentor... This link opens in a new window, ID Ajlec, Tomaž (Comentor)

.pdfPDF - Presentation file, Download (2,44 MB)
MD5: FB3FC3950F42767E9CE81FC1E9884D9E
PID: 20.500.12556/rul/215110df-8d68-4ad0-83dd-526cf2533058

Language:Slovenian
Keywords:aluminijeva zlitina, tlačno litje, mehanske lastnosti, karakterizacija
Work type:Bachelor thesis/paper
Organization:NTF - Faculty of Natural Sciences and Engineering
Place of publishing:Ljubljana
Publisher:[M. Sovinc]
Year:2017
Number of pages:VI, 37 f.
PID:20.500.12556/RUL-94461 This link opens in a new window
UDC:669.2/.8
COBISS.SI-ID:1666143 This link opens in a new window
Publication date in RUL:29.08.2017
Views:10802
Downloads:731
Metadata:XML DC-XML DC-RDF
:
SOVINC, Martina, 2017, Karakterizacija zlitine AlSi7Mg0,3 : diplomsko delo [online]. Bachelor’s thesis. Ljubljana : M. Sovinc. [Accessed 9 June 2025]. Retrieved from: https://repozitorij.uni-lj.si/IzpisGradiva.php?lang=eng&id=94461
Copy citation
Share:Bookmark and Share

Secondary language

Language:English
Keywords:aluminium alloy, die-casting, mechanical properties, characterization

Similar documents

Similar works from RUL:
  1. Vpliv pogojev staranja na trdoto izločevalno utrjevalnega nerjavnega jekla 17-4 PH
  2. Vpliv stopnje deformacije na mehanske lastnosti hladno vlečenega jekla PT929
  3. Razvoj mikrostrukture in mehanskih lastnosti jekla UTOPNICu
  4. Vpliv toplotne obdelave na izločevalno utrjevanje nerjavnega jekla 17-4 PH
  5. Optimizacija toplotne obdelave zlitine A356.0
Similar works from other Slovenian collections:
  1. Influence of density on mechanical properties of high density PM steel
  2. Določitev parametrov mehanike loma za zvar iz jekla AISI 304
  3. Weldability of microalloyed high strength steels TStE 420 and S960QL
  4. Odziv mehanskih lastnosti na mikrostrukturne spremembe jekla 16MnCrS5
  5. Tensile test models for low-carbon microalloyed steels with high niobium contents

Back