Vpliv ohlajevalne hitrosti na mikrostrukturo jekla GS20Mn5 : diplomsko delo
ID Miljković, Edin (Author), ID Markoli, Boštjan (Mentor) More about this mentor... This link opens in a new window

.pdfPDF - Presentation file, Download (3,30 MB)
MD5: 5422CFD7384E786E805FBF5E413947BC
PID: 20.500.12556/rul/ab15b441-4006-4893-9326-e911dc8ce8bb

Language:Slovenian
Keywords:jeklo GS20Mn5, ohlajevalna hitrost, mikrotrdota, EDS analiza, fazna analiza
Work type:High school thesis
Typology:2.11 - Undergraduate Thesis
Organization:NTF - Faculty of Natural Sciences and Engineering
Place of publishing:Ljubljana
Publisher:[E. Miljković]
Year:2015
Number of pages:VIII, 39 f.
PID:20.500.12556/RUL-81105 This link opens in a new window
UDC:669.1
COBISS.SI-ID:1585247 This link opens in a new window
Publication date in RUL:29.03.2016
Views:2760
Downloads:1041
Metadata:XML DC-XML DC-RDF
:
MILJKOVIĆ, Edin, 2015, Vpliv ohlajevalne hitrosti na mikrostrukturo jekla GS20Mn5 : diplomsko delo [online]. Bachelor’s thesis. Ljubljana : E. Miljković. [Accessed 20 March 2025]. Retrieved from: https://repozitorij.uni-lj.si/IzpisGradiva.php?lang=eng&id=81105
Copy citation
Share:Bookmark and Share

Secondary language

Language:English
Keywords:GS20Mn5 steel, cooling rate, microhardness, EDS analysis, phase analysis

Similar documents

Similar works from RUL:
  1. Fizikalno-metalurški vidiki vpliva elementov na tvorbo kvazikristalov v zlitinah Al-Mn
  2. Karakterizacija zlitine AlSi7Mg0,3
  3. Nadzorovana tvorba kvazikristalov v zlitinah Al-Mn
  4. Application of massive laser shock processing for improvement of mechanical and tribological properties
  5. Varjenje z gnetenjem aluminijeve zlitine 2030
Similar works from other Slovenian collections:
  1. Vpliv ohlajevalne hitrosti na mikrostrukturo zlitine Al-Mn-Be
  2. Vpliv toplotne obdelave na lastnosti orodnih jekel
  3. Vpliv toplotne obdelave na mikrostrukturo in lastnosti WC-10Co4Cr prevlek, izdelanih z zelo hitrim naprševanjem vplinski atmosferi mešanice propana in zraka
  4. Mikrostruktura hitro strjenih trakov zlitine Cu-Zr
  5. Wear resistance of coke-crushing hammers

Back