Fizikalno-metalurški vidiki vpliva elementov na tvorbo kvazikristalov v zlitinah Al-Mn : magistrsko delo
ID Leskovar, Blaž (Author), ID Naglič, Iztok (Mentor) More about this mentor... This link opens in a new window

.pdfPDF - Presentation file, Download (12,77 MB)
MD5: 69D4811D6FD29121E91F4D8862E264DD
PID: 20.500.12556/rul/d2aac45a-db9c-4fda-8564-3fe0478d2488

Language:Slovenian
Keywords:kvazikristali, ulivanje, aluminijeve zlitine, morfologija, mikrostruktura
Work type:Bachelor thesis/paper
Typology:2.09 - Master's Thesis
Organization:NTF - Faculty of Natural Sciences and Engineering
Place of publishing:Ljubljana
Publisher:[B. Leskovar]
Year:2015
Number of pages:XVI, 55 f.
PID:20.500.12556/RUL-73358 This link opens in a new window
UDC:669
COBISS.SI-ID:1557087 This link opens in a new window
Publication date in RUL:04.11.2015
Views:4594
Downloads:515
Metadata:XML DC-XML DC-RDF
:
LESKOVAR, Blaž, 2015, Fizikalno-metalurški vidiki vpliva elementov na tvorbo kvazikristalov v zlitinah Al-Mn : magistrsko delo [online]. Master’s thesis. Ljubljana : B. Leskovar. [Accessed 29 March 2025]. Retrieved from: https://repozitorij.uni-lj.si/IzpisGradiva.php?lang=eng&id=73358
Copy citation
Share:Bookmark and Share

Secondary language

Language:English
Keywords:quasicrystals, casting, aluminium alloys, morphology, microstructure

Similar documents

Similar works from RUL:
  1. Razvoj nove livarske aluminijeve zlitine z dodatkom litija
  2. Influence of Zirconium nad Molybdenum on mechanical properties of alloy Silafont-36
  3. influence of input material on solidification, microstructure and mechanical properties of AlSi12 and AlSi10Mg alloys
  4. Izdelava in predelava zlitine EN AW 6082 z dodatkom cirkonija
  5. Controlled formation of quasicrystals in Al-Mn alloys
Similar works from other Slovenian collections:
  1. Influence of the working technology on the development of alloys H13-w(Cu) 87.5 %
  2. Quasicrystal-strengthened cast Al-alloys
  3. Evolution of microstructure and embrittlement during the tempering process in SiCrCu medium-carbon steels
  4. The effect of heat treatment on the interface of 155 PH martensitic stainless steel and SAF 2507 duplex steel in functionally graded AM components

Back