The diploma thesis includes an analysis of the influence of the substrate on adhesion of the material in additive manufacturing by the process of targeted polymer loading method. A Creality CR10 printer using the FDM method was used. To analyze the adhesion of the material, the plate was printed at different substrate temperatures and with different adhesives. Six different prints were made. First, three tiles were printed on three different substrates without adhesives, then all three substrates were printed with three different adhesives. Analysis of the tiles was performed under a VHX-6000 microscope. It was found that the tile printed with the Dimafix adhesive was the best approximation to the ideal print, also in terms of aesthetics and removal of the tile from the hot plate after printing.
|