Vpliv zaščitnega plina pri laserskem varjenju avstenitnega nerjavnega jekla
ID Filipčič, Rok (Author), ID Klobčar, Damjan (Mentor) More about this mentor... This link opens in a new window

.pdfPDF - Presentation file, Download (4,18 MB)
MD5: 1AA1FFC774BD1DFB6691FC08469C25A2

Abstract
Zaključna naloga obravnava preverjanje vpliva zaščitnega plina pri laserskem varjenju avstenitnega nerjavnega jekla. Glavni razlog je pocenitev proizvodnega procesa z uporabo cenejšega zaščitnega plina dušika namesto argona. Kakovost izdelanih zvarov smo testirali vizualno, s tlačno-strižnim preizkusom in z metalografsko analizo. Ugotovili smo, da je zaščitni plin dušik dobra alternativa argonu. Po vizualni kontroli smo ugotovili, da nastane lep zvar, s tlačno-strižnim preizkusom smo dokazali, da lahko tak var zdrži obremenitve v uporabi, z metalografsko analizo pa smo pokazali, da nam tako definiran postopek zagotavlja zahtevano globino zavaritve.

Language:Slovenian
Keywords:lasersko varjenje, avstenitno nerjavno jeklo, tlačno-strižni preizkus, vizualna kontrola, metalografska analiza
Work type:Bachelor thesis/paper
Typology:2.11 - Undergraduate Thesis
Organization:FS - Faculty of Mechanical Engineering
Place of publishing:Ljubljana
Publisher:[R. Filipčič]
Year:2020
Number of pages:XX, 54 str.
PID:20.500.12556/RUL-118835 This link opens in a new window
UDC:621.791.7:691.714.018.8(043.2)
COBISS.SI-ID:29203459 This link opens in a new window
Publication date in RUL:01.09.2020
Views:1720
Downloads:371
Metadata:XML DC-XML DC-RDF
:
FILIPČIČ, Rok, 2020, Vpliv zaščitnega plina pri laserskem varjenju avstenitnega nerjavnega jekla [online]. Bachelor’s thesis. Ljubljana : R. Filipčič. [Accessed 17 March 2025]. Retrieved from: https://repozitorij.uni-lj.si/IzpisGradiva.php?lang=eng&id=118835
Copy citation
Share:Bookmark and Share

Secondary language

Language:English
Title:Effect of shielding gas in laser welding of austenitic stainless steel
Abstract:
The final thesis discusses the influence of shielding gasses during laser welding of austenitic stainless steel. The main reason for conducting this research is the reduction of the production process costs, using a cheaper shielding gas nitrogen instead of argon. The quality of welds was tested using visually, with a pressure-shear testing and metallographic analysis. It was found that shielding gas nitrogen is a good alternative to argon. Visual inspection proved the quality of weld appearance. Pressure-shear test we proved the mechanical strength of the weld and metallographic analysis sufficient penetration depth. It was concluded that argon shielding gas can be exchanged with nitrogen at laser welding of austenitic stainless steel.

Keywords:laser welding, austenitic stainless steel, pressure-shear test, visual control, metallographic analysis

Similar documents

Similar works from RUL:
  1. Fotokatalitska razgradnja antibiotika tetraciklina s tankimi plastmi titanovega dioksida
  2. Pretočni fotokatalitski reaktorji za čiščenje vode
  3. Sinteza in karakterizacija fotokatalitsko aktivnega mezoporoznega TiO [spodaj] 2 z dodatkom CeO [spodaj] 2
  4. Fotokatalitske lastnosti prozornih tankih plasti dopiranega TiO [spodaj] 2 z vanadijem v silikatnem vezivu
  5. Nanos TiO [spodaj] 2 fotokatalizatorja na milimetrske granule
Similar works from other Slovenian collections:
  1. Zr/Cu-TiO[sub]2 catalysts for photocatalytic water treatment
  2. Optimizacija tankih plasti titanovega dioksida na aluminiju za namene fotokatalitskega čiščenja vode
  3. Porozni hibridni materiali iz sistema monomer/TiO[spodaj]2
  4. Spremljanje reoloških lastnosti anorganskih prahov
  5. Vpliv izbranih UV-filtrov na rast celic malignega melanoma

Back