ID Žos, Rok (Author), ID Šturm, Roman (Mentor) More about this mentor... This link opens in a new window

.pdfPDF - Presentation file, Download (4,96 MB)
MD5: 632DF032EA3EBD04621D8F5C0B1943E0

Abstract
Namen diplomskega dela je bil izdelati damaščansko kompozitno jeklo ter ga skovati v vzorce primerne za mehanske preizkuse. V diplomskem delu smo kovaško zvarili damaščansko jeklo iz jekel 15N20 in S235JR. Na pripravljenih vzorcih smo opravili udarni test žilavosti, upogibni preizkus, test trdote ter preučili mikrostrukturo. Vzorci so imeli različno število plasti in bili različno toplotno obdelani. Vzorci so bili kaljeni v olju, kaljeni v dveh sredstvih ter kaljeni v olju in popuščani v peči. Ugotovili smo, da trdota narašča s povečevanjem hitrosti ohlajanja in ne s številom slojev. Največji upogibni raztezek smo dosegli na vzorcu kaljenem v olju in na zraku ter ugotovili, da se vrednosti upogibnega raztezka zmanjšujejo z naraščanjem števila slojev kompozita.

Language:Slovenian
Keywords:maloogljično jeklo, evtektoidno jeklo, kovaško varjenje, trdota, udarna žilavost, mikrostruktura
Work type:Bachelor thesis/paper (mb11)
Typology:2.11 - Undergraduate Thesis
Organization:FS - Faculty of Mechanical Engineering
Year:2020
Publisher:[R. Žos]
Number of pages:XVIII, 45 str.
PID:20.500.12556/RUL-113498 This link opens in a new window
UDC:621.791.42:669.14:539.4(043.2)
COBISS.SI-ID:17030939 This link opens in a new window
Publication date in RUL:11.01.2020
Views:854
Downloads:183
Metadata:XML RDF-CHPDL DC-XML DC-RDF
:
Kopiraj citat
Share:AddThis
AddThis uses cookies that require your consent. Edit consent...

Secondary language

Language:English
Title:Strength characteristics of metal welded steel
Abstract:
The purpose of diploma thesis is to forge damascus composit steel and forge it into samples for mechanical tests. In my thesis we forge welded damascus steel from 15N20 and S235JR steels. On prepared samples we did Charpy impact test, deflection test, hardness test and studied the microstructure. The samples had different number of layers and were differently heat treated. They were quenched in oil, quenched in oil and air and some were quenched in oil and then tempered in furnace to release internal stresses. We figured out that the speed of heat treatment has the biggest influence on hardness. The highest value of deflection appeared when we heat treated the sample in oil and air. Deflection was decreasing when we increased the number of layers of composit.

Keywords:low carbon steel, evtectoid steel, forge welding, hardness, impact toughness, microstructure