This thesis examines the problem of protecting the metal parts of the transformer before assembly. In the introduction, areas where problems most occurred were identified. It was found that the greatest number of defects occurred in parts, which are not protected by anti-corrosion paint due to further processing. Alternative possibilities of corrosion protection were researched, evaluated and then the most appropriate were selected. Selected solutions were then tested for their effectiveness. Instructions are presented, defining how the metal parts of the transformer must be protected and packaged, so that they do not change their properties during storage.
|