Vpliv parametrov injekcijskega brizganja polimera ABS na natezno trdnost materiala
Zakšek, Ana (Author), Pepelnjak, Tomaž (Mentor) More about this mentor... This link opens in a new window

.pdfPDF - Presentation file, Download (4,30 MB)

V diplomski nalogi so predstavljeni parametri za injekcijsko brizganje polimerov. Opisan je postopek injekcijskega brizganja. Predstavljen je material akrilonitril butadien stiren (ABS), ki je bil uporabljen za eksperimentalni del. Opisan je postopek nateznega preizkusa in prikaz natezne trdnosti za ABS material. Rezultati so slikovno in grafično prikazani ter opisani. V zaključku so predstavljene najboljše kombinacije parametrov za uspešno brizganje in izboljšanje natezne trdnosti materiala.

Keywords:akrilonitril butadien stiren (ABS), injekcijsko brizganje, natezni preizkus, polimer, parametri, natezna trdnost
Work type:Final paper (mb12)
Tipology:2.11 - Undergraduate Thesis
Organization:FS - Faculty of Mechanical Engineering
Publisher:[A. Zakšek]
COBISS.SI-ID:16248347 Link is opened in a new window
Average score:(0 votes)
Your score:Voting is allowed only to logged in users.
AddThis uses cookies that require your consent. Edit consent...

Secondary language

Title:Influence of injection moulding parameters on tensile strength of ABS polymer
This thesis focuses on parameters for injection molding of polymers. The method of injection molding itself and the material acrylonitrile butadiene styrene (ABS), which was used for the experimental part, are presented. The thesis also describes the procedure of tensile testing and tensile strength for ABS material. All of the results are graphically presented and explained. In conclusion the best combinations of parameters for successful spraying and improvement of the tensile strength of the material are presented.

Keywords:acrylonitrile butadiene styrene (ABS), injection moulding, tensile test, polymer, parameters, tensile strength

Similar documents

Similar works from RUL:
Similar works from other Slovenian collections:


Leave comment

You have to log in to leave a comment.

Comments (0)
0 - 0 / 0
There are no comments!