Vpliv ohlajevalne hitrosti na mikrostrukturo jekla GS20Mn5 : diplomsko delo
ID Miljković, Edin (Author), ID Markoli, Boštjan (Mentor) More about this mentor... This link opens in a new window

.pdfPDF - Presentation file, Download (3,30 MB)
MD5: 5422CFD7384E786E805FBF5E413947BC
PID: 20.500.12556/rul/ab15b441-4006-4893-9326-e911dc8ce8bb

Language:Slovenian
Keywords:jeklo GS20Mn5, ohlajevalna hitrost, mikrotrdota, EDS analiza, fazna analiza
Work type:High school thesis
Typology:2.11 - Undergraduate Thesis
Organization:NTF - Faculty of Natural Sciences and Engineering
Place of publishing:Ljubljana
Publisher:[E. Miljković]
Year:2015
Number of pages:VIII, 39 f.
PID:20.500.12556/RUL-81105 This link opens in a new window
UDC:669.1
COBISS.SI-ID:1585247 This link opens in a new window
Publication date in RUL:29.03.2016
Views:2825
Downloads:1060
Metadata:XML DC-XML DC-RDF
:
MILJKOVIĆ, Edin, 2015, Vpliv ohlajevalne hitrosti na mikrostrukturo jekla GS20Mn5 : diplomsko delo [online]. Bachelor’s thesis. Ljubljana : E. Miljković. [Accessed 29 March 2025]. Retrieved from: https://repozitorij.uni-lj.si/IzpisGradiva.php?lang=eng&id=81105
Copy citation
Share:Bookmark and Share

Secondary language

Language:English
Keywords:GS20Mn5 steel, cooling rate, microhardness, EDS analysis, phase analysis

Similar documents

Similar works from RUL:
  1. Razvoj nove livarske aluminijeve zlitine z dodatkom litija
  2. Influence of Zirconium nad Molybdenum on mechanical properties of alloy Silafont-36
  3. influence of input material on solidification, microstructure and mechanical properties of AlSi12 and AlSi10Mg alloys
  4. Izdelava in predelava zlitine EN AW 6082 z dodatkom cirkonija
  5. Controlled formation of quasicrystals in Al-Mn alloys
Similar works from other Slovenian collections:
  1. Vpliv tehnologije izdelave na razvoj zlitine H13-w(Cu) 87,5 %
  2. Aluminijeve livne zlitine, utrjene s kvazikristali
  3. Razvoj mikrostrukture in krhkosti srednje ogljičnega jekla vrste SiCrCu med njegovim postopkom popuščanja
  4. The effect of heat treatment on the interface of 155 PH martensitic stainless steel and SAF 2507 duplex steel in functionally graded AM components

Back