Vpliv toplotne obdelave na mikrostrukturo zlitine iz sistema Al-Si-Mg-Zr : diplomsko delo
ID Oblak, Luka (Author), ID Mrvar, Primož (Mentor) More about this mentor... This link opens in a new window

.pdfPDF - Presentation file, Download (2,17 MB)
MD5: C4D037EFDB374C1FA04D099EAC7ACBE4
PID: 20.500.12556/rul/e4a675cf-4e6f-4453-89da-091108c71726

Language:Slovenian
Keywords:zlitina Al-Si-Mg-Zr, toplotna obdelava, homogenizacijsko žarjenje, ohlajevalna hitrost, mikrostruktura
Work type:Final paper
Typology:2.11 - Undergraduate Thesis
Organization:NTF - Faculty of Natural Sciences and Engineering
Place of publishing:Ljubljana
Publisher:[L. Oblak]
Year:2015
Number of pages:VI, 36 f.
PID:20.500.12556/RUL-73348 This link opens in a new window
UDC:669.2/.8
COBISS.SI-ID:1562207 This link opens in a new window
Publication date in RUL:04.11.2015
Views:3357
Downloads:514
Metadata:XML DC-XML DC-RDF
:
OBLAK, Luka, 2015, Vpliv toplotne obdelave na mikrostrukturo zlitine iz sistema Al-Si-Mg-Zr : diplomsko delo [online]. Bachelor’s thesis. Ljubljana : L. Oblak. [Accessed 29 March 2025]. Retrieved from: https://repozitorij.uni-lj.si/IzpisGradiva.php?lang=eng&id=73348
Copy citation
Share:Bookmark and Share

Secondary language

Language:English
Keywords:Al-Si-Mg-Zr alloy, heat treatment, homogenization, cooling rate, microstructure

Similar documents

Similar works from RUL:
  1. development of new cast aluminium alloy with lithium addition
  2. Vpliv cirkonija in molibdena na mehanske lastnosti zlitine Silafont-36
  3. Vpliv vhodnega materiala na strjevanje, mikrostrukturo in mehanske lastnosti zlitin AlSi12 in AlSi10Mg
  4. Izdelava in predelava zlitine EN AW 6082 z dodatkom cirkonija
  5. Nadzorovana tvorba kvazikristalov v zlitinah Al-Mn
Similar works from other Slovenian collections:
  1. Vpliv tehnologije izdelave na razvoj zlitine H13-w(Cu) 87,5 %
  2. Aluminijeve livne zlitine, utrjene s kvazikristali
  3. Razvoj mikrostrukture in krhkosti srednje ogljičnega jekla vrste SiCrCu med njegovim postopkom popuščanja
  4. The effect of heat treatment on the interface of 155 PH martensitic stainless steel and SAF 2507 duplex steel in functionally graded AM components

Back