Tvorba kvazikristalov v Al-Mn zlitinah z dodatki Ca, Cr, Si, Sr, Zn, in Zr : diplomsko delo
ID Zaky, Adam (Author), ID Naglič, Iztok (Mentor) More about this mentor... This link opens in a new window

.pdfPDF - Presentation file, Download (7,75 MB)
MD5: 82C377E8E0E40038F3766EC2D0D64929
PID: 20.500.12556/rul/84639b90-c4cd-41ba-b5ba-79967fb36517

Language:Slovenian
Keywords:aluminijeva zlitina, kvazikristali, ulivanje, mikrostruktura
Work type:Bachelor thesis/paper
Typology:2.11 - Undergraduate Thesis
Organization:NTF - Faculty of Natural Sciences and Engineering
Place of publishing:Ljubljana
Publisher:[A. Zaky]
Year:2015
Number of pages:V, 39 f.
PID:20.500.12556/RUL-73338 This link opens in a new window
UDC:669.2/.8
COBISS.SI-ID:1559647 This link opens in a new window
Publication date in RUL:04.11.2015
Views:3050
Downloads:341
Metadata:XML DC-XML DC-RDF
:
ZAKY, Adam, 2015, Tvorba kvazikristalov v Al-Mn zlitinah z dodatki Ca, Cr, Si, Sr, Zn, in Zr : diplomsko delo [online]. Bachelor’s thesis. Ljubljana : A. Zaky. [Accessed 31 March 2025]. Retrieved from: https://repozitorij.uni-lj.si/IzpisGradiva.php?lang=eng&id=73338
Copy citation
Share:Bookmark and Share

Secondary language

Language:English
Keywords:aluminium alloy, quasicrystals, casting, microstructure

Similar documents

Similar works from RUL:
  1. Vpliv pogojev staranja na trdoto izločevalno utrjevalnega nerjavnega jekla 17-4 PH
  2. Vpliv stopnje deformacije na mehanske lastnosti hladno vlečenega jekla PT929
  3. Razvoj mikrostrukture in mehanskih lastnosti jekla UTOPNICu
  4. Vpliv toplotne obdelave na izločevalno utrjevanje nerjavnega jekla 17-4 PH
  5. Optimizacija toplotne obdelave zlitine A356.0
Similar works from other Slovenian collections:
  1. Influence of density on mechanical properties of high density PM steel
  2. Določitev parametrov mehanike loma za zvar iz jekla AISI 304
  3. Weldability of microalloyed high strength steels TStE 420 and S960QL
  4. Odziv mehanskih lastnosti na mikrostrukturne spremembe jekla 16MnCrS5
  5. Tensile test models for low-carbon microalloyed steels with high niobium contents

Back