Sinteza oksida z visoko entropijo (Ni$_{0,2}$Mg$_{0,2}$Co$_{0,2}$Cu$_{0,2}$Zn$_{0,2}$)O brez uporabe topil

Levičar, Maks (avtor), Skalar, Tina (mentor)

Visoko entropijski oksidi so posebna skupina keramičnih materialov, za katere je veliko zanimanja zaradi njihovih prilagodljivih lastnosti ter uporabnosti v katalizi in za shranjevanje energije. V tem delu se po metodi uporabe topil sintetizira visoko entropijski oksid s sestavo (Ni$_{0,2}$Mg$_{0,2}$Co$_{0,2}$Cu$_{0,2}$Zn$_{0,2}$)O, ki se ureja v halitno kristalno strukturo. Produkt je karakteriziran s praškovno rentgensko difrakcijo, energijsko disperzijsko analizo in je slikan z vrstičnim elektronskim mikroskopom. Poleg končnega produkta je bil z XRD ovrednotena tudi sušena reakcijska mešanica v vmesni fazi pred kalcinacijo. Zaželen je homogen produkt, pri katerem so se vsi reagenti združili v enovito strukturo znotraj iste kristalne mreže. Pri optimizaciji sinteze za nastanek ciljnega produkta so se preizkušali naslednji parametri: pogoji mletja (čas in število vrtljajev na minuto) ter čas in temperatura kalcinacije. Pri zadostno visoki temperaturi kalcinacije je tak produkt uspešno nastal.

• Jezik: Slovenski jezik
• Ključne besede: visoko entropijski materiali, visoko entropijski oksid, sinteza brez uporabe topil.
• Vrsta gradiva: Magistrsko delo/naloga
• Tipologija: 2.09 - Magistrsko delo
• Organizacija: FKKT - Fakulteta za kemijo in kemijsko tehnologijo
• Leto izida: 2024
• PID: 20.500.12556/RUL-162446
• COBISS.SI-ID: 216092931
• Datum objave v RUL: 23.09.2024

Sekundarni jezik

• Jezik: Angleški jezik
• Naslov: Synthesis of high entropy oxide (Ni$_{0,2}$Mg$_{0,2}$Co$_{0,2}$Cu$_{0,2}$Zn$_{0,2}$)O using solvent deficient method

Izvleček

High entropy oxides are a special group of ceramic materials that are held in high interest due to their highly adjustable properties and their use in catalysis and energy storage. In this thesis, a high entropy oxide with the composition (Ni$_{0,2}$Mg$_{0,2}$Co$_{0,2}$Cu$_{0,2}$Zn$_{0,2}$)O with a halite crystal structure is synthesized using a solvent-deficient method. The product is characterized using powder x-ray diffraction and energy dispersive spectroscopy and is imaged using a scanning electron microscope. Aside from the final product, the dried reaction mixture in an intermediate stage before the calcination has been evaluated using XRD. The target product is a homogenous one where all the reagents have fully combined into a single structure within the same crystal lattice. During the optimization of synthesis to produce a desirable product, the following parameters have been tested: milling time and speed (revolutions per minute), time and temperature of calcination. At a sufficiently high calcination temperature, such a product has been successfully created.

• Ključne besede: high entropy materials, high entropy oxide, solvent deficient synthesis method.