Influence of austempering of as-cast medium carbon high-silicon steel on wear resistance

Sedlaček, Marko (avtor), Klančnik, Grega (avtor), Nagode, Aleš (avtor), Burja, Jaka (avtor)

The aim of this study was to evaluate the effect of austempering compared to quenching and low-temperature tempering on wear resistance of an as-cast medium carbon high-silicon steel intended for rock breaking. Austempering was done by isothermal holding at 270, 300 and 350 °C in molten salt baths, while quenching was done in water. The austempering treatments resulted in microstructural combinations of bainite and martensite. The isothermal holding at 270 °C resulted in bainite and self-tempered martensite, while isothermal holdings at 300 and 350 °C resulted in bainite and untempered martensite. The two quench and temper treatments resulted in tempered martensite. In general austempering resulted in lower hardness values when compared to quenching and tempering but higher impact toughness. The wear resistance was best for quenching and low temperature tempering, followed by austempering at 270 °C, but at slightly lower hardness and 25% higher impact toughness. The other two austempering treatments resulted in worse wear resistance.

• Jezik: Angleški jezik
• Ključne besede: austempering wear, lower bainite, wear, impact toughness, hardness
• Vrsta gradiva: Članek v reviji
• Tipologija: 1.01 - Izvirni znanstveni članek
• Organizacija: NTF - Naravoslovnotehniška fakulteta
• Status publikacije: Objavljeno
• Različica publikacije: Objavljena publikacija
• Leto izida: 2021
• Št. strani: 12 str.
• Številčenje: Vol. 14, iss. 24, art. 7518
• PID: 20.500.12556/RUL-136686
• UDK: 620.1:669.1:67.017
• ISSN pri članku: 1996-1944
• DOI: 10.3390/ma14247518
• COBISS.SI-ID: 88748035
• Datum objave v RUL: 16.05.2022

Gradivo je del revije

• Naslov: Materials
• Skrajšan naslov: Materials
• Založnik: Molecular Diversity Preservation International
• ISSN: 1996-1944
• COBISS.SI-ID: 33588485

Licence

• Licenca: CC BY 4.0, Creative Commons Priznanje avtorstva 4.0 Mednarodna
• Povezava: http://creativecommons.org/licenses/by/4.0/deed.sl
• Opis: To je standardna licenca Creative Commons, ki daje uporabnikom največ možnosti za nadaljnjo uporabo dela, pri čemer morajo navesti avtorja.
• Začetek licenciranja: 08.12.2021

Projekti

• Financer: ARRS - Agencija za raziskovalno dejavnost Republike Slovenije
• Številka projekta: P2-0050
• Naslov: Kovinski materiali in tehnologije