Characterization of the AZ31/AW-6060 joint fabricated using compound casting with a Zn interlayer at relatively low temperature conditions
ID
Bucki, Tomasz
(
Avtor
),
ID
Konieczny, Marek
(
Avtor
),
ID
Bolibruchová, Dana
(
Avtor
),
ID
Rzepa, Sylwia
(
Avtor
)
PDF - Predstavitvena datoteka,
prenos
(5,07 MB)
MD5: 917856C33877CA227522AF2F979BBAC3
URL - Izvorni URL, za dostop obiščite
https://www.sv-jme.eu/sl/article/characterisation-of-the-az31aw-6060-joint-fabricated-by-compound-casting-with-a-zn-interlayer-at-relatively-low-temperature-conditions/
Galerija slik
Izvleček
The work deals with the fabrication of a joint between AZ31 magnesium alloy and AW-6060 aluminium alloy with the use of a Zn interlayer. The Zn layer was produced on the surface of an AW-6060 alloy insert by diffusion bonding. The insert was then placed inside a steel mould and kept at room temperature. The joint was produced using compound casting by filling the mould with liquid AZ31 alloy, heated to 650 °C. The microstructure of the bonding zone formed between joined alloys was analysed using an optical microscope and a scanning electron microscope equipped with an energy dispersive X-ray spectroscope. The properties of the joint were examined using Vickers microhardness measurements and simple shear strength testing. As a result of the experiment, the 400 [micro]m thick bonding zone with a complex microstructure was formed between the alloys. The microstructural analysis showed that the bonding zone reveals a high concentration of Zn and Mg. The layers of a eutectoid (a MgZn phase + a solid solution of Al and Zn in Mg), a Mg5Al2Zn2 phase and a Mg(Al,Zn)2 phase with fine particles of other phases were observed there. The bonding zone was characterized by relatively high microhardness, which was related to the brittleness of the constituents. The shear strength of the examined joint was 19.6 +/- 2.5 MPa.
Jezik:
Angleški jezik
Ključne besede:
compound casting
,
magnesium alloys
,
aluminium alloys
,
zinc interlayer
,
microstructures
,
mechanical properties
Vrsta gradiva:
Članek v reviji
Tipologija:
1.01 - Izvirni znanstveni članek
Organizacija:
FS - Fakulteta za strojništvo
Status publikacije:
Objavljeno
Različica publikacije:
Objavljena publikacija
Leto izida:
2021
Št. strani:
Str. 389-397
Številčenje:
Vol. 67, no. 7/8
PID:
20.500.12556/RUL-130973
UDK:
621.74:669.721.5+669.715
ISSN pri članku:
0039-2480
DOI:
10.5545/sv-jme.2021.7262
COBISS.SI-ID:
76913411
Datum objave v RUL:
20.09.2021
Število ogledov:
1109
Število prenosov:
128
Metapodatki:
Citiraj gradivo
Navadno besedilo
BibTeX
EndNote XML
EndNote/Refer
RIS
ABNT
ACM Ref
AMA
APA
Chicago 17th Author-Date
Harvard
IEEE
ISO 690
MLA
Vancouver
:
Kopiraj citat
Objavi na:
Gradivo je del revije
Naslov:
Strojniški vestnik
Skrajšan naslov:
Stroj. vestn.
Založnik:
Zveza strojnih inženirjev in tehnikov Slovenije [etc.], = Association of Mechanical Engineers and Technicians of Slovenia [etc.
ISSN:
0039-2480
COBISS.SI-ID:
762116
Sekundarni jezik
Jezik:
Slovenski jezik
Naslov:
Karakterizacija spoja AZ31/AW-6060, izdelanega po postopku sestavljenega litja z vmesno plastjo Zn pri razmeroma nizkih temperaturah
Ključne besede:
sestavljeno litje
,
magnezijeve zlitine
,
aluminijeve zlitine
,
cinkova vmesna plast
,
mikrostrukture
,
mehanske lastnosti