Analysis and prevention of weld crater cracking in circumferential laser microwelding of automotive pressure sensors

Kenda, Miha (avtor), Klobčar, Damjan (avtor), Nagode, Aleš (avtor), Bračun, Drago (avtor)

An analysis presents a weld leakage problems of automotive pressure sensor, caused by weld crater cracking. A two-beam laser welding (TBLW) was used to weld a circumferential weld, which undesirably increases the probability of weld leakage by creating two weld end craters on a single weld. Microstructural analysis showed that microsegregation of alloying elements combined with imposed strains causes solidification cracking at the weld end crater. A novel "zigzag" laser power ramp-down was used and the results showed a limited crack propagation by producing significantly shorter discontinuous cracks. In such weld crater endings the leakage is no longer an issue.

• Jezik: Angleški jezik
• Ključne besede: two-beam laser welding, continuous-wave, solidification cracking, weld termination regime, ramp-down, lap joint, 17–4 PH steel, Inconel 602
• Vrsta gradiva: Članek v reviji
• Tipologija: 1.01 - Izvirni znanstveni članek
• Organizacija: FS - Fakulteta za strojništvo ; NTF - Naravoslovnotehniška fakulteta
• Status publikacije: Objavljeno
• Različica publikacije: Objavljena publikacija
• Leto izida: 2021
• Št. strani: 14 str.
• Številčenje: Vol. 128, art. 105579
• PID: 20.500.12556/RUL-128354
• UDK: 621.791.725
• ISSN pri članku: 1350-6307
• DOI: 10.1016/j.engfailanal.2021.105579
• COBISS.SI-ID: 69793539
• Datum objave v RUL: 09.07.2021

Gradivo je del revije

• Naslov: Engineering failure analysis
• Skrajšan naslov: Eng fail. anal.
• Založnik: Elsevier
• ISSN: 1350-6307
• COBISS.SI-ID: 15354117

Licence

• Licenca: CC BY 4.0, Creative Commons Priznanje avtorstva 4.0 Mednarodna
• Povezava: http://creativecommons.org/licenses/by/4.0/deed.sl
• Opis: To je standardna licenca Creative Commons, ki daje uporabnikom največ možnosti za nadaljnjo uporabo dela, pri čemer morajo navesti avtorja.

Sekundarni jezik

• Jezik: Slovenski jezik
• Ključne besede: lasersko varjenje z dvojnim žarkom, kontinuirno varjenje, razpoke v vročem, zaključevanje laserskih zvarov, zaključna rampa, prekrovni spoj, 17-4 PH, Inconel 602

Projekti

• Financer: Drugi - Drug financer ali več financerjev
• Program financ.: Hidria Holding d.o.o.

• Financer: ARRS - Agencija za raziskovalno dejavnost Republike Slovenije
• Številka projekta: P2-0270
• Naslov: Proizvodni sistemi, laserske tehnologije in spajanje materialov