Development of Fe-Si-B powders for soft-magnetic application
Godec, Matjaž (Avtor), Mandrino, Djordje (Avtor), Šuštaršič, Borivoj (Avtor), Jenko, Monika (Avtor), Prešern, Vasilij (Avtor)

URLURL - Predstavitvena datoteka, za dostop obiščite http://www.dlib.si/details/URN:NBN:SI:DOC-8XBHVZFZ Novo okno

Izvleček
Soft magnetic composite (SMC) materials based on Fe-Si-B powder have been developed. The most important property of SMC materials, especially those used in a high-frequency range, is that the soft-magnetic powder particles are well insulated from each other. The Fe-Si-B powders were prepared by water-atomisation and were compared with some commercially available powders. The surfaces of microcrystalline powders were investigated using high-resolution Auger-electron spectroscopy (HRAES) and X-ray photoelectron spectroscopy (XPS). The electrical break-down voltages, permeability and electrical losses of SMC materials were measured.

Jezik:Angleški jezik
Ključne besede:SMC, Fe-Si-B, insulating layer, XPS, AES
Vrsta gradiva:Delo ni kategorizirano (r6)
Tipologija:1.01 - Izvirni znanstveni članek
Organizacija:NTF - Naravoslovnotehniška fakulteta
Leto izida:2001
Založnik:Inštitut za kovinske materiale in tehnologije
Št. strani:str. 325-330
Številčenje:Letn. 35, št. 6
UDK:669.018.95:669.1:621.318.1
ISSN pri članku:1580-2949
COBISS.SI-ID:324959 Povezava se odpre v novem oknu
Število ogledov:329
Število prenosov:121
Metapodatki:XML RDF-CHPDL DC-XML DC-RDF
 
Skupna ocena:(0 glasov)
Vaša ocena:Ocenjevanje je dovoljeno samo prijavljenim uporabnikom.
:
Objavi na: Bookmark and Share

Gradivo je del revije

Naslov:Materiali in tehnologije
Skrajšan naslov:Mater. tehnol.
Založnik:Inštitut za kovinske materiale in tehnologije
ISSN:1580-2949
COBISS.SI-ID:106193664 Novo okno

Sekundarni jezik

Jezik:Slovenski jezik
Naslov:Razvoj prahov na osnovi Fe-Si-B za mehkomagnetne materiale
Izvleček:
Na osnovi prahu Fe-Si-B smo razvili mehkomagnetne kompozitne materiale. Če so namenjeni za uporabo v visokofrekvenčnem področju, morajo imeti zelo dobro izolacijo med posameznimi delci-prahovi. Prahove Fe-Si-B smo pripravili po postopku vodne atomizacije in jih primerjali z nekaterimi komercialnimi. Površine mikrokristaliničnih prahov smo preiskali z visoko ločljivim Augerjevim elektronskim spektrometrom (HR AES) in z rentgenskim fotoelektronskim spektrometrom (XPS). Izmerili smo tudi nekatere električne lastnosti mehkomagnetnih kompozitov, kot so: električna prebojna napetost, permeabilnost in električne izgube.

Ključne besede:SMC, Fe-Si-B, izolacijska plast, XPS, AES

Podobna dela

Podobna dela v RUL:
Podobna dela v drugih slovenskih zbirkah:

Komentarji

Dodaj komentar

Za komentiranje se morate prijaviti.

Komentarji (0)
0 - 0 / 0
 
Ni komentarjev!

Nazaj