The influence of microstruture on fracture toughness of vacuum heat treated HSS AISI M2
Leskovšek, Vojteh (Author), Ule, Boris (Author), Liščić, Božidar (Author)

URLURL - Presentation file, Visit http://www.dlib.si/details/URN:NBN:SI:DOC-BEND4OFK This link opens in a new window

Abstract
The microstructure of AISI M2 high-speed can be substantially modified by vacuum heat treatment in order to optimize the ratio between hardness and fracture toughness, which is, however, significantly affected by the volume fractions of retained austenite and undissolved eutectic carbides, as well as the mean distance between these carbides. Calculated fracture toughness values, which were obtained using a newly developed semi-empirical equation, based on the stress-modified critical strain criterion and the quantified microstructural parameters, agreed well with the experimental results.

Language:English
Keywords:vacuum heat treatment, high speed steel, quantified microstructural parameters, hardness and fracture toughness
Work type:Not categorized (r6)
Tipology:1.01 - Original Scientific Article
Organization:NTF - Faculty of Natural Sciences and Engineering
Year:2001
Publisher:Inštitut za kovinske materiale in tehnologije
Number of pages:str. 211-217
Numbering:Letn. 35, št. 5
UDC:621.785:669.14.018.252.3:620.18:539.55
ISSN on article:1580-2949
COBISS.SI-ID:306271 Link is opened in a new window
Views:429
Downloads:117
Metadata:XML RDF-CHPDL DC-XML DC-RDF
 
Average score:(0 votes)
Your score:Voting is allowed only to logged in users.
:
Share:AddThis
AddThis uses cookies that require your consent. Edit consent...

Record is a part of a journal

Title:Materiali in tehnologije
Shortened title:Mater. tehnol.
Publisher:Inštitut za kovinske materiale in tehnologije
ISSN:1580-2949
COBISS.SI-ID:106193664 This link opens in a new window

Secondary language

Language:Slovenian
Title:Vpliv mikrostrukture na lomno žilavost vakuumsko toplotno obdelanega hitroreznega jekla M2
Abstract:
Opisano je optimiranje vakuumske toplotne obdelave hitroreznega jekla M2. Po vakuumski toplotni obdelavi takšnega jekla je večji delež zaostalega avstenita, avstenitna zrna so večja, njihove kristalne meje pa so močneje markirane s precipitati karbidov kot pa v primeru konvencionalne toplotne obdelave v solni kopeli. Volumski delež neraztopljenih evtektičnih karbidov jev takšnem jeklu odvisen le od temperature avstenitizacije. Mikrofraktografska opazovanja so pokazala, da iniciranje loma v relativno trdem in krhkem hitroreznem jeklu poteka tudi z delno koalescenco mikropor. Lomno žilavost takšnega jekla smo opisali z modificirano obliko kritičnega napetostnega kriterija, ki upošteva tudi vpliv mikrostrukturnih parametrov: volumskega deleža neraztopljenih evtektičnih karbidov in srednje razdalje med njimi ter volumeskega deleža yaostalega avstenita. Delež tega avstenita je numerično skoraj enak eksponentu deformacijskega utrjevanja jekla. Vpliv napetosti tečenja in lomne duktilnosti pa smo izrazili s trdoto jekla. Ker je velikost plastične cone pri merjenju lomne žilavosti tega jekla praviloma manjša od velikosti kristalnih zrn, le ta ne vplivajo na lomno žilavost. Izkazalo se je, da se po naši enačbi izračunane lomne žilavosti dobro ujemajo tako z našimi eksperimentalnimi podatki in tistimi iz literature.

Keywords:vakuumska toplotna obdelava, hitrorezno jeklo, mikrostruktura, trdota, lomna žilavost, dimenzijske spremembe

Similar documents

Similar works from RUL:
Similar works from other Slovenian collections:

Comments

Leave comment

You have to log in to leave a comment.

Comments (0)
0 - 0 / 0
 
There are no comments!

Back