A co-precipitation procedure for the synthesis of LSM material
Marinšek, Marjan (Avtor), Zupan, Klementina (Avtor), Razpotnik, Tanja (Avtor), Maček, Jadran (Avtor)

URLURL - Predstavitvena datoteka, za dostop obiščite http://www.dlib.si/details/URN:NBN:SI:DOC-A0ICAPFI Povezava se odpre v novem oknu

Izvleček
Lanthanum manganite substituted with strontium is a strong candidate for use as a mixed conductor at the cathode site in solid-oxide fuel-cell systems. In the present work a co-precipitation method for the preparation of LSM is described and some material properties are reported. Since the co-precipitation involved calcination at 1000 °C and subsequent sintering, the crystalline phase development and the material homogeneity were followed by X-ray powder diffraction. It was found that no secondary crystalline phases were present in the system when the samples were thermally treated up to 1200 °C. The sintering behaviour of the calcined powders and their density evolution are also reported. Relatively dense bodies were prepared after thermal treatment at 1200 °C for 2 hours. The electrical characteristics of the material were determined from screen-printed LSM sintered layers. The electrical conductivity of the screen-printed layers increased with the sintering temperature due to an additional densification effect. Porous LSM bodies were prepared by methyl cellulose admixing as a pore-former.

Jezik:Angleški jezik
Ključne besede:co-precipitation, lanthanum strontium manganite, microstructure, electrical conductivity
Vrsta gradiva:Delo ni kategorizirano (r6)
Tipologija:1.01 - Izvirni znanstveni članek
Organizacija:FKKT - Fakulteta za kemijo in kemijsko tehnologijo
Leto izida:2007
Založnik:Inštitut za kovinske materiale in tehnologije
Št. strani:str. 85-90
Številčenje:Letn. 41, št. 2
UDK:661.871:620.18
ISSN pri članku:1580-2949
COBISS.SI-ID:603562 Povezava se odpre v novem oknu
Število ogledov:642
Število prenosov:179
Metapodatki:XML RDF-CHPDL DC-XML DC-RDF
 
Skupna ocena:(0 glasov)
Vaša ocena:Ocenjevanje je dovoljeno samo prijavljenim uporabnikom.
:
Objavi na:AddThis
AddThis uporablja piškotke, za katere potrebujemo vaše privoljenje.
Uredi privoljenje...

Gradivo je del revije

Naslov:Materiali in tehnologije
Skrajšan naslov:Mater. tehnol.
Založnik:Inštitut za kovinske materiale in tehnologije
ISSN:1580-2949
COBISS.SI-ID:106193664 Povezava se odpre v novem oknu

Sekundarni jezik

Jezik:Slovenski jezik
Naslov:Sobarjanje LSM za pripravo katodnih materialov za gorivne celice
Izvleček:
Najpogosteje uporabljan katodni material v visokotemperaturni izvedbi gorivnih celic (SOFC) je lantanov manganit, dopiran s stroncijem (LSM). LSM s sestavo La[spodaj]{0,85}Sr[spodaj]{0,15}MnO[spodaj]{3-d} smo priprav[!]li z novo metodo soobarjanja iz raztopine karbonatov. Oborino smo po filtraciji in spiranju sušili pri 110 °C in nato kalcinirali pri 1000 °C. Po kalcinaciji pri različnih temperaturah in po sintranju smo prahove analizirali z rentgensko praškovno analizo. Materialiso po sintranju vsebovali le perovskitno kristalno obliko lantanovega manganita. Parametre sintranja prahov LSM po kalcinaciji pri 1000 °C smo določili s segrevalnim mikroskopom. Vzorce LSM z dodatkom tvorca por in brez njega smo po sintranju analizirali z elektronsko mikroskopijo. Električne karakteristike tiskanih plasti LSM smo določili s štiritočkovno metodo. Specifična električna prevodnost pripravljenih plasti LSM je primerljiva z literaturnimi podatki za materiale LSM, ki so bili pripravljeni po kalcinacijskem postopku.

Ključne besede:koprecipitacija, lantanov stroncijev manganit, katoda, mikrostruktura, električna prevodnost

Podobna dela

Podobna dela v RUL:
Podobna dela v drugih slovenskih zbirkah:

Komentarji

Dodaj komentar

Za komentiranje se morate prijaviti.

Komentarji (0)
0 - 0 / 0
 
Ni komentarjev!

Nazaj