Phase relations in the Pt-Ag17.5-Si4.5 ternary alloy
Klančnik, Grega (Avtor), Mrvar, Primož (Avtor), Medved, Jožef (Avtor)

URLURL - Predstavitvena datoteka, za dostop obiščite http://www.imt.si/Revija/ Novo okno

Izvleček
An investigation of the Pt-Ag17.5-Si4.5 ternary alloy was carried out. Thermodynamic data on platinum systems are scarce and are mostly based on binary systems. No accurate thermodynamic study of the Pt-Ag-Si ternary system has been published so far. Thermodynamic calculations were used as an indication of the possible phase composition for the investigated platinum-based alloy. The results are based on differential scanning calorimetry (DSC) tests, scanning electron microscopy with energy-dispersive X-ray spectroscopy (SEM - EDS) and X-ray diffraction measurements (XRD). The analyses revealed the presence of two phases that were found after homogenization at 900 °C: a high-temperature phase, Pt[sub]{2}Si, and a Ag (Pt) solid solution.

Jezik:Angleški jezik
Ključne besede:Pt-Ag-Si alloys, thermal analysis, thermodynamics
Vrsta gradiva:Delo ni kategorizirano (r6)
Tipologija:1.01 - Izvirni znanstveni članek
Organizacija:NTF - Naravoslovnotehniška fakulteta
Leto izida:2010
Založnik:Inštitut za kovinske materiale in tehnologije
Št. strani:Str. 213-217
Številčenje:Vol. 44, no. 4
UDK:536:543.57:546.92 57 28
ISSN pri članku:1580-2949
COBISS.SI-ID:820906 Povezava se odpre v novem oknu
Število ogledov:359
Število prenosov:90
Metapodatki:XML RDF-CHPDL DC-XML DC-RDF
 
Skupna ocena:(0 glasov)
Vaša ocena:Ocenjevanje je dovoljeno samo prijavljenim uporabnikom.
:
Objavi na: Bookmark and Share

Gradivo je del revije

Naslov:Materiali in tehnologije
Skrajšan naslov:Mater. tehnol.
Založnik:Inštitut za kovinske materiale in tehnologije
ISSN:1580-2949
COBISS.SI-ID:106193664 Novo okno

Sekundarni jezik

Jezik:Slovenski jezik
Naslov:Fazna odvisnost v ternarni zlitini Pt-Ag17.5-Si4.5
Izvleček:
V tem prispevku je opisana raziskava, ki je osredinjena na ternarno zlitino Pt-Ag17.5-Si4.5. Za zlitinske sisteme, ki so osnovani na platini, so termodinamski podatki skopi in temeljijo predvsem na binarnih faznih sistemih. Nobena termodinamska študija še ni bila opravljena na ternarnem sistemu Pt-Ag-Si. Za izbiro ustrezne kemijske sestave smo uporabili termodinamski izračun. Prvi rezultati so bili dobljeni z diferenčno vrstično kalorimetrijo (DSC), rastrskim elektronskim mikroskopom z energijsko disperzivno rentgensko spektroskopijo (SEM - EDS) in rentgensko analizo (XRD). Analize so potrdile obstoj dveh binarnih faz, dobljeni po homogenizaciji na 900 °C. Najdeni fazi sta visokotemperaturna faza Pt[spodaj]{2}Si in trdna raztopina na osnovi srebra Ag (Pt).

Ključne besede:Pt-Ag-Si zlitine, Termična analiza, termodinamika

Podobna dela

Podobna dela v RUL:
Podobna dela v drugih slovenskih zbirkah:

Komentarji

Dodaj komentar

Za komentiranje se morate prijaviti.

Komentarji (0)
0 - 0 / 0
 
Ni komentarjev!

Nazaj