Residual stresses on flat specimens of different kinds of grey and nodular irons after laser surface remelting
Grum, Janez (Author), Šturm, Roman (Author)

URLURL - Presentation file, Visit http://www.materials.org.uk/publish/journals/mst/contents.htm New window

Abstract
Laser surface remelting is one of the best procedures for surface modification of ferrite-pearlite nodular irons. Using this procedure on cast irons it is possible to achieve a very high wear resistance, which can be compared with the wear resistance of surface hardened heat treatable steels. The properties of the modified layer depend on the microstructure before heat treatment and on the amount of energy input transferred into the surface layer of the specimen. The research work was focused on the study of residual stresses after laser surface remelting of different kinds of gray and nodular irons. The identification of residual stresses was performed using the relaxation method, which involved measuring specimen strain. The results of the measured residual stresses confirm that the stresses strongly depend on the laser surface remelting conditions. The measurement of residual stresses is very important in exacting dynamically loaded machine parts, which have been subjected to different kinds of heat treatment. In designing parts designers very frequently demand the presence of compressive residual stresses after heat treatment and finish grinding of the surface, since this increases the fatigue strength of the material and reduces the danger of fracture.

Language:English
Keywords:surface modification, laser surface remelting, residual stresses, flat specimens, cast irons, grey irons, nodular irons
Work type:Not categorized (r6)
Tipology:1.01 - Original Scientific Article
Organization:FS - Faculty of Mechanical Engineering
Year:2001
Number of pages:str. 419-424
Numbering:Vol. 17, no. 4
UDC:620.1/.2:621.791
ISSN on article:0267-0836
COBISS.SI-ID:4332827 Link is opened in a new window
Views:380
Downloads:123
Metadata:XML RDF-CHPDL DC-XML DC-RDF
 
Average score:(0 votes)
Your score:Voting is allowed only to logged in users.
:
Share: Bookmark and Share

Record is a part of a journal

Title:Materials science and technology
Shortened title:Mater. sci. technol.
Publisher:Institute of Metals
ISSN:0267-0836
COBISS.SI-ID:5989125 New window

Similar documents

Similar works from RUL:
Similar works from other Slovenian collections:

Comments

Leave comment

You have to log in to leave a comment.

Comments (0)
0 - 0 / 0
 
There are no comments!

Back