20.500.12556/RUL-99022 Corrosion on polished and laser-textured surfaces of an Fe-Mn biodegradable alloy Primerjava korozijskih lastnosti polirane in lasersko teksturirane površine biorazgradljive zlitine Fe-Mn Fe-based biodegradable alloys such as Fe-Mn are interesting for biodegradable implants; however, their corrosion rate for such applications is too low. Here, nanosecond-laser surface texturing is applied as a successful surface treatment for increasing the degradation rate of an Fe-Mn alloy. Laser texturing increases the surface area by increasing the surface porosity and generating a super-hydrophilic surface. Electrochemistry tests revealed that the laser-textured samples have a higher corrosion rate than a polished sample, thus enhancing the biodegradability of the Fe-Mn alloy. EDS analyses revealed a significantly higher content of Mn on the surface in the oxidized layer compared to the bulk Fe-Mn composition, which is one of the reasons for the increased corrosion rate. This work demonstrates the potential of laser-treated surfaces of biodegradable metals for biomedical applications. Biološko razgradljive zlitine, kot so na primer Fe-Mn zlitine, so zanimive za uporabo v obliki biološko razgradljivih implantantov, vendar je njihova hitrost korozije za ciljne aplikacije še vedno prenizka. Lasersko teksturiranje površine predstavlja uspešno površinsko obdelavo za povečanje hitrosti razgradnje Fe-Mn zlitine. Obdelava površine z laserjem poveča delež izpostavljene površine na račun večje poroznosti, obenem pa je novonastala površina superhidrofilna. Elektrokemijski testi so pokazali, da imajo vzorci, obdelani z laserjem, večjo stopnjo korozije v primerjavi s poliranimi vzorci, s čimer se poveča biorazgradljivost zlitine Fe-Mn. EDS analiza je pokazala povečano vsebnost Mn na površini v oksidirani plasti v primerjavi s kemijsko sestavo osnovnega materiala Fe-Mn, kar predstavlja eno od razlag za povečanje hitrosti korozije. Raziskava dokazuje potencial laserske obdelave površine biološko razgradljivih kovin za biomedicinske aplikacije. Fe-Mn alloy laser texturing corrosion biodegradable EDS analyses zlitina Fe-Mn lasersko teksturiranje korozija biorazgradljivost EDS analiza true false false Angleški jezik Slovenski jezik Neznano 2017-12-21 07:48:35 2018-02-14 11:36:50 2025-03-06 12:16:24 0000-00-00 00:00:00 2017 0 0 Str. 1037-1041 št. 6 Letn. 51 2017 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 620.1/.2(045) 1580-2949 10.17222/mit.2017.140 15804187 106193664 hocevar.pdf hocevar.pdf 1 009AB5B381BD81427D03F9C6A4FC6F78 816f36817434fdf03d8332d6f27db7682cec65409177a0f86c6f3e306a9eb68d a9e4b4b9-a1b4-11eb-a523-00155dcfd717 20.500.12556/rul/6c3d3f95-1d12-4f0d-bf53-27fa740c6c54 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=109685 http://mit.imt.si/izvodi/mit176/hocevar.pdf 0 796a9fdc-fa7b-11ef-b232-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=200395 Fakulteta za strojništvo 0 0 0