20.500.12556/RUL-478 Vpliv vrednosti pH termično modificiranega lesa na utrjevanje lepil diplomsko delo - univerzitetni študij Influence of pH value of thermally modified wood on curing of adhesives graduation thesis - university studies Termična modifikacija lesa vpliva na znižanje vrednosti pH, kar lahko povzroča težave pri lepljenju modificiranega lesa z različnimi lepili. Da bi raziskali dejanski vpliv pH vrednosti lesa na utrjevanje lepil, smo v raziskavi zlepili 2 vrsti termično obdelanega lesa ter kontrolni, nemodificiran les. Iz lesa smo pripravili lamele, ki smo jih zlepili z urea-formaldehidnim (UF) in fenol formaldehidnim (FF) lepilom. Mehanske lastnosti lepilnega spoja smo preskušali s strižnim testom (SIST-TS CEN/TS 13354:2004). Spreminjanje reoloških lastnosti lepila med utrjevanjem smo spremljali z reometrom, stopnjo utrjenosti lepila pa z dielektrično analizo. Strižni moduli sistema les-lepilo se pri lepljenju z UF niso bistveno razlikovali, večje razlike pa so se pokazale pri lepljenju s FF lepilom. Dielektrična analiza je pokazala večjo začetno hitrost utrjevanja UF in FF lepila pri lepljenju modificiranega lesa, a je končna utrditev v obeh primerih najprej nastopila pri kontrolnem lesu. Največjo strižno trdnost lepilnega spoja smo ugotovili pri termično modificiranem lesu. Strižna trdnost se pri lepljenju s FF, v primerjavi z UF, ni zmanjšala, temveč se je v večini primerov celo nekoliko povečala. Izkazalo se je tudi, da sprememba vrednosti pH, zaradi termične modifikacije, ni vplivala na utrjevanje FF lepila, saj je bilo lepilo dovolj bazično in ni dopustilo večje spremembe vrednosti pH. Thermal modification of wood causes decrease of pH value, causing problems while gluing such wood with different types of glues. To research the actual influence we have glued lamellas of 2 different stages of modification and one non-treated sample with 2 different glues, (UF and PF). A shear test (SIST-TS CEN/TS 13354:2004) has been used to test the mechanical properties, rheometer to test the rheological properties and dielectric analysis to measure glue curing. The results show that shear modules of a system (wood-glue) do not differ essentially when gluing with UF. However, gluing with PF shows bigger differences. Dielectric analysis results show higher curing velocity at the beginning of the test at heat treated samples. Shear strength is the best at heat treated wood and does not decrease when gluing with PF; in most samples it even increases. In our case the pH decreased while thermal treatment did not have any influence on curing capacity of PF glue. The glue used was too alkaline, so we could not influence the pH of the curing medium. lepljenje termično modificiran les vrednost pH reologija utrjevanje dielektrična analiza mehanske lastnosti gluing thermally modified wood pH value rheology curing dielectric analysis mechanical properties true false false [M. Čop] Slovenski jezik Angleški jezik Diplomsko delo 2014-07-11 12:25:46 2014-07-11 12:25:46 2022-07-11 10:26:43 0000-00-00 00:00:00 2009 0 Ljubljana 0 X, 65 f., [5] f. pril. 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 630*824.86 1782409 dn_cop_matjaz.pdf dn_cop_matjaz.pdf 1 E55AFC286E0D06580ABB0B14C42CF58B 674cac84e48a2ce329e999101fbea516d07f2e00fff0c994d2a2527aec4e7fdb 605d8730-a1b9-11eb-a523-00155dcfd717 20.500.12556/rul/0ea53cdb-f498-4e36-a50b-138200c93377 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=132354 Biotehniška fakulteta 0 0 0