20.500.12556/RUL-187969 Performance of hydroxyapatite mineralised beech and pine wood wettability and biological This study investigates the effects of hydroxyapatite (HAp) mineralisation on the water-related properties and biological resistance of beech and pine wood. As HAp synthesis also produces the highly water-soluble by-product NH4NO3, particular emphasis was placed on comparing unleached and leached samples to distinguish the effects of HAp and NH4NO3. During outdoor exposure, HAp effectively inhibited mould and blue stain fungi. In laboratory mould tests, this effect was observed only in leached samples, suggesting that the HAp mineral layer contributes to protection by physically blocking the wood pores. Fungal decay tests showed a significant improvement in unleached HAp-synthesised samples, with the highest median Δm value for B-HAp samples at 6.4% and for P-HAp samples at 5.6%; both corresponded to durability class 2. In contrast, leached samples showed lower resistance, with beech and pine classified in durability classes 4 (Δm for B-HAp-L 20.4%) and 3 (Δm for P-HAp-L 11.8%), respectively. However, the soil contact test showed limited protection for all HAp synthesised samples. Overall, using the Meyer–Veltrup model, mineralisation with HAp was found to improve DRd rel. factors for pine in both leached and unleached samples, with values of 4.7 and 4.4, respectively. HAp synthesised beech samples showed comparable improvements (DRd rel. = 4.1), although these were considerably smaller in the leached samples (DRd rel. = 1.8). Higher DRd rel. factors resulted from improved decay resistance, as HAp treatment did not improve water-related properties. durability resistance hydroxyapatite leaching mineralised wood wettability obstojnost hidroksiapatit izpiranje mineraliziran les močljivost true false true Angleški jezik Slovenski jezik Članek v reviji 2026-09-17 07:52:02 2026-09-17 07:52:07 2026-09-18 04:30:28 0000-00-00 00:00:00 2026 0 0 Str. 1-15 atricle 148197 Vol. 543 0000-00-00 Zaloznikova Objavljeno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 630*8 0950-0618 10.1016/j.conbuildmat.2026.148197 291318019 RAZ_Sitar_Matic_2026.pdf RAZ_Sitar_Matic_2026.pdf 1 37FFFE89A7DA7438DFFE666710859034 972e57f0b147578580c763dc656d4fa565fd4268491bc9e57dab66d235afd720 404506d0-b25c-11f1-8bc5-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=247819 https://www.sciencedirect.com/science/article/pii/S0950061826031065 1 e0a5102c-b25b-11f1-8bc5-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=247818 Biotehniška fakulteta 0 0 0