20.500.12556/RUL-186990 Vpliv oblikovanja vzorca na oksetični potencial žakarske tkanine Influence of pattern design on the auxetic potential of jacquard fabric V diplomski nalogi je bil raziskan vpliv geometrije vzorca, razporeditve in zasuk elementov vzorca, gostote votka in uporabe preje iz polibutilentereftalata (PBT) na razvoj oksetičnega potenciala žakarskih tkanin. Načrtovanih in izdelanih je bilo enajst žakarskih tkanin z različnimi geometrijami vzorcev. Vzorci so bili načrtovani s pomočjo računalniško podprtega sistema Arahne ter stkani na žakarskem tkalskem stroju z bombažno osnovo pri enakih konstrukcijskih parametrih in različnih votkovnih prejah. Po izdelavi so bile na vzorcih določene spremembe dimenzij, gostota niti, debelina, zračna prepustnost in natezne lastnosti pred toplotn obdelavo in po njej. Oksetični potencial tkanin je bil ovrednoten z določitvijo Poissonovega števila na podlagi nateznih preizkusov in slikovne analize. Rezultati so pokazali, da geometrija in oblika vzorca pomembno vplivata na oksetično obnašanje žakarskih tkanin, medtem ko vpliv zasuka oziroma razporeditve geometrijskih elementov ni bil bistven. Pri uporabi preje v votku iz polibutilentereftalata so se po toplotni obdelavi tkanine skrčile v prečni smeri, nastala je tridimenzionalna reliefna struktura in izboljšal se je oksetični odziv. Rezultati so bili najboljši pri vzorcu z enakomerno porazdeljeno kvadratno geometrijo in PBT prejo po votku, izkazana je bila največja negativna vrednost Poissonovega števila in ohranjeno oksetično obnašanje v najširšem območju deformacij. Poleg tega so se po toplotni obdelavi spremenile tudi debelina, dimenzije in zračna prepustnost tkanin. Ugotovljeno je bilo, da je za razvoj funkcionalnih oksetičnih žakarskih tkanin ključna predvsem ustrezna kombinacija geometrije vzorca in uporabe preje iz polibutilentereftalata, medtem ko zasuk elementov vzorca nima pomembnega vpliva na razvoj oksetičnega učinka. Rezultati so izhodišče za nadaljnji razvoj oksetičnih tekstilnih struktur za uporabo na področju funkcionalnih in tehničnih tekstilij. In the thesis, the influence of pattern geometry, the arrangement and pattern rotation, weft density, and the use of polybutylene terephthalate (PBT) yarn on the auxetic potential of Jacquard woven fabrics was investigated. Eleven Jacquard woven fabrics with different pattern geometries were designed and produced. The fabrics were created using the Arahne computer-aided design system and woven on a Jacquard weaving machine with the same cotton warp and identical constructional parameters, while different weft yarns and weft densities were used. After weaving, dimensional changes, density, thickness, air permeability, and tensile properties were determined before and after heat treatment. The auxetic potential of the fabrics was evaluated by determining Poisson's ratio based on tensile testing and image analysis. The results showed that pattern geometry and shape significantly affected the auxetic behaviour of the Jacquard woven fabrics, whereas the pattern rotation and arrangement of the pattern elements had no significant influence. The use of polybutylene terephthalate (PBT) yarn in the weft caused transverse shrinkage during heat treatment, resulting in the formation of a three dimensional textured structure and an improved auxetic response. Among all the samples investigated, the fabric with a uniformly distributed square geometry and PBT weft yarn exhibited the best performance, achieving the highest negative Poisson's ratio and maintaining auxetic behaviour over the widest strain range. Heat treatment also affected the density, athickness, dimensions, and air permeability of the fabrics. It was concluded that the development of functional auxetic Jacquard woven fabrics primarily depends on an appropriate combination of pattern geometry and the use of polybutylene terephthalate yarn, whereas the orientation of the pattern elements has no significant influence on the development of the auxetic effect. The results obtained provide a basis for the further development of auxetic textile structures intended for functional and technical textile applications. oksetične tkanine žakarske tkanine Poissonovo število geometrija vzorca polibutilentereftalat (PBT) bombaž auxetic woven fabrics Jacquard woven fabrics Poisson's ratio pattern geometry polybutylene terephthalate (PBT) cotton true false false Slovenski jezik Angleški jezik Diplomsko delo/naloga 2026-09-08 09:01:19 2026-09-08 09:01:25 2026-09-09 04:22:15 0000-00-00 00:00:00 2026 0 0 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 1970-01-01 116058 30365.pdf 30365.pdf 1 AE4FB34E3C47058537E3C3D1383E2B43 774ce764b0e1d01b63ee4121aa79e0b981c66d0300237e8ce591bc016562407a 16f8de75-ab53-11f1-8bc5-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=246401 Naravoslovnotehniška fakulteta 0 0 0