20.500.12556/RUL-186722 Razvoj ometov z dodatkom fazno spremenljivih materialov za izboljšanje bivanjskega udobja Development of plasters with the addition of phase-change materials to improve living comfort V diplomskem delu smo razvili apneno-cementni omet z dodatkom fazno spremenljivega materiala PCM 22 in njegove lastnosti primerjali z referenčnim ometom brez dodatka PCM. Preučili smo lastnosti svežih in strjenih ometnih mešanic, mikrostrukturo, mehanske lastnosti ter toplotno obnašanje materiala. Dodatek PCM je zmanjšal prostorninsko maso in gostoto ometa ter povečal njegovo razlivnost, hkrati pa sta se zmanjšali upogibna in tlačna trdnost. Mikroskopska analiza je pokazala manj kompaktno strukturo vzorca z dodatkom PCM. Pri določanju specifične toplotne kapacitete je bil v območju med približno 22 in 24 °C zaznan izrazit fazni prehod. Pri 23 °C je bila navidezna specifična toplotna kapaciteta vzorca z dodatkom PCM za 165,4 % večja od vrednosti referenčnega ometa. Rezultati potrjujejo, da PCM tudi po vgradnji v omet ohrani sposobnost shranjevanja toplote, vendar je pri nadaljnjem razvoju treba izboljšati razmerje med toplotno funkcionalnostjo in mehansko odpornostjo materiala. In this thesis, a lime-cement plaster containing the phase change material PCM 22 was developed and compared with a reference plaster without PCM. The properties of fresh and hardened plaster mixtures, their microstructure, mechanical properties and thermal behaviour were investigated. The addition of PCM reduced the bulk density and density of the plaster and increased its flow value, while the flexural and compressive strengths decreased. Microscopic analysis showed a less compact structure of the PCM-containing specimen. Specific heat capacity measurements revealed a pronounced phase transition between approximately 22 and 24 °C. At 23 °C, the apparent specific heat capacity of the PCM-containing plaster was 165.4 % higher than that of the reference plaster. The results confirm that PCM retains its heat-storage ability after being incorporated into the plaster. However, further development is required to achieve an appropriate balance between thermal functionality and mechanical resistance. fazno spremenljivi materiali apneno-cementni omet specifična toplotna kapaciteta shranjevanje toplote mehanske lastnosti phase change materials lime-cement plaster specific heat capacity thermal energy storage mechanical properties true false false Slovenski jezik Angleški jezik Diplomsko delo/naloga 2026-09-04 09:05:00 2026-09-04 09:05:03 2026-09-06 03:32:57 0000-00-00 00:00:00 2026 0 0 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 1970-01-01 26088 Venko_Timon_-_Razvoj_ometov_z_dodatkom_fazno_spremenljivih_materialov_za_izboljsanje_bivanjskega.pdf Venko_Timon_-_Razvoj_ometov_z_dodatkom_fazno_spremenljivih_materialov_za_izboljsanje_bivanjskega.pdf 1 7DADB130E4D08B9D7D7527F3CC14CF93 2a829a899188d3edfa16d7df53e527725200836346d48449cbb7e28d492dcc58 f30a51e0-a82e-11f1-8bc5-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=246061 Fakulteta za kemijo in kemijsko tehnologijo 0 0 0