20.500.12556/RUL-186691 Vpliv naknadne obdelave površine na trajno dinamično trdnost dodajalno izdelanih komponent Influence of surface post-processing on the fatigue strength of additively manufactured parts Trajna dinamična trdnost dodajalno izdelanih kovinskih komponent je močno odvisna od kakovosti njihove površine, ki je v stanju brez obdelave razmeroma hrapava. V zaključni nalogi smo eksperimentalno ovrednotili vpliv plazemskega elektrolitskega poliranja na trajno dinamično trdnost ploščatih vzorcev iz nerjavnega jekla X2CrNiMo17-12-2 (AISI 316L), izdelanih s spajanjem slojev praškastega materiala z laserskim snopom (PBF-LB). Pripravili smo dve skupini po petnajst vzorcev: v eni so vzorci brez obdelave, v drugi pa smo jih plazemsko elektrolitsko polirali. Stanje površine smo popisali s profilnimi in ploskovnimi parametri hrapavosti, ter s parametri Abbottove krivulje nosilnosti, ki smo jih izmerili z dotikalnim merilnikom MarSurf PS 10 in digitalnim mikroskopom Keyence VHX6000. Obe skupini smo primerjali z nateznimi preizkusi in s preizkusi osnega utrujanja pri razmerju napetosti R = −1. Poliranje je srednji aritmetični odstopek profila zmanjšalo s 6,93 µm na 0,43 µm, torej za približno 94 %, natezne mehanske lastnosti pa so ostale praktično nespremenjene. Polirani vzorci so pri enakih amplitudah napetosti dosegli približno dvakrat večje število ciklov do porušitve, kot neobdelani vzorci, le pri najvišjih obremenitvah se je prednost izgubila. Rezultati potrjujejo, da plazemsko elektrolitsko poliranje pomembno izboljša odpornost dodajalno izdelanega nerjavnega jekla proti utrujanju. The fatigue strength of additively manufactured metal parts strongly depends on the quality of their surface, which is relatively rough in the as-built state. In this thesis, the effect of plasma electrolytic polishing on the fatigue strength of flat X2CrNiMo17-12-2 (AISI 316L) stainless steel specimens, produced by laser powder bed fusion (PBF-LB), was evaluated experimentally. Two groups of specimens were prepared, each with fifteen specimens: one in the as-built state and the other treated by plasma electrolytic polishing. The surface condition was characterised by profile and areal roughness parameters and by the parameters of the Abbott bearing-area curve, measured with a MarSurf PS 10 stylus instrument and a Keyence VHX-6000 digital microscope. The two groups were compared by tensile tests and by axial fatigue tests at a stress ratio of R = −1. Polishing reduced the arithmetic mean roughness of the profile from 6.93 µm to 0.43 µm, i.e. by approximately 94 %, while the tensile mechanical properties remained practically unchanged. At equal stress amplitudes, the polished specimens reached approximately twice the number of cycles to failure, except at the highest load levels. The results confirm that plasma electrolytic polishing considerably improves the fatigue resistance of additively manufactured stainless steel. trajna dinamična trdnost naknadna obdelava površine plazemsko elektrolitsko poliranje dodajalna izdelava nerjavno jeklo AISI 316L površinska hrapavost Abbottova krivulja nosilnosti krivulja S-N fatigue strength surface post-processing plasma electrolytic polishing additive manufacturing AISI 316L stainless steel surface roughness Abbott bearing-area curve S-N curve true false false [V. Božičevič] Slovenski jezik Angleški jezik Diplomsko delo/naloga 2026-09-04 08:31:35 2026-09-04 08:31:39 2026-09-08 13:25:31 0000-00-00 00:00:00 2026 0 Ljubljana 0 XI, 32 f. 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 621.793:621.791:620.178.3(043.2) 289188 290388995 49106.pdf 49106.pdf 1 B7073DB76ABD7D1909E34D55B9DE6AE6 4897506c0b68894cc5a1f190ed559eb302f8ed413200737aad56ff223a015261 47dd7a67-a82a-11f1-8bc5-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=246013 Fakulteta za strojništvo 0 0 0