20.500.12556/RUL-186275 Izdelava papirja z večjo vsebnostjo kratkih vlaken ob ohranitvi fizikalno-mehanskih lastnosti Production of paper with higher content of short fibres while maintaining physical-mechanical properties Za izdelavo kakovostnega papirja, ki je ustrezno odporen na obremenitve, so potrebni dobri začetni pogoji njegove izdelave. Papirno maso sestavljajo različne vrste celuloznih vlaken, ki zaradi želje po doseganju različnih končnih značilnosti vsebujejo tako dolga kot kratka vlakna. Daljša vlakna prispevajo k večji mehanski odpornosti, medtem ko kratka vlakna izboljšujejo površinsko gladkost in formacijo papirja. Namen naloge je predstaviti, kaj se zgodi z določenimi fizikalno-mehanskimi lastnostmi papirja v primerih, ko vključujemo večje deleže kratkih vlaken pri treh različnih načinih industrijskega mletja. V teoretičnem delu so predstavljeni papir, surovine za njegovo izdelavo, papirna vlakna in njihova priprava, proces izdelave papirja ter njegove ključne fizikalno-mehanske lastnosti. Eksperimentalni del diplomskega dela je bil opravljen v Papirnici Vevče, kjer so bili izdelani vsi papirni vzorci in izmerjene njihove ključne fizikalno-mehanske lastnosti. Osredotočili smo se na meritve poroznosti, upogibne togosti, raztržne odpornosti, razpočne odpornosti, natezne trdnosti in natezne trdnosti po pregibu. Rezultati meritev so opredeljeni v dveh delih. V prvem delu smo prikazali izmerjene vrednosti glede na način mletja celuloznih vlaken, v drugem delu pa smo definirali odvisnost vsakega parametra od sestave papirne mase in načina mletja začetnih celuloznih vlaken. Ugotovljeno je bilo, da takšno razmerje uporabljenih dolgih in kratkih vlaken kot tudi način mletja celuloznih vlaken vplivata na ključne fizikalno-mehanske lastnosti papirja. Ustrezna izbira začetnih surovin močno vpliva na lastnosti končnih izdelkov in zagotavlja učinkovitost proizvodnega procesa papirne industrije. Čeprav bi povečanje deleža kratkih vlaken lahko prispevalo k boljši optimizaciji procesov papirne industrije, njihova prekomerna uporaba ni primerna, saj povzroča preveliko poslabšanje lastnosti končnih papirnih izdelkov. For high-quality paper that is sufficiently resistant to loads, good initial conditions are required for its production. Paper pulp consists of various types of cellulose fibres, which, to achieve different final characteristics, include both long and short fibres. Longer fibres provide greater mechanical resistance, while short fibres improve surface smoothness and paper formation. The purpose of this thesis is to present how certain physical and mechanical properties of paper change when large proportions of short fibres are included using three different industrial milling methods. The theoretical section covers paper, raw materials for its production, paper fibres and their preparation, the paper production process, and its key physicaland mechanical properties. The experimental part of the thesis was conducted at Papirnica Vevče, where all paper samples were produced and their key physicaland mechanical properties were measured. We focused on measurements of porosity, bending stiffness, tearing resistance, bursting strength, tensile strength, and tensile strength after bending. The measurement results are presented in two sections. In the first section, we display the measured values according to the pulp grinding method, while in the second section, we present the dependence of each parameter on the composition of the paper stock and the method of grinding the initial pulp. It was found that both the ratio of long to short fibres used and the method of pulp grinding affect the key physicaland mechanical properties of paper. The appropriate choice of starting raw materials strongly influences the properties of the final products and ensures the efficiency of the paper industry production process. Although increasing the proportion of short fibres could contribute to better optimization of paper industry processes, their excessive use is not appropriate, as it still results in an overestimation of the properties of the final paper products. celulozna vlakna kratka vlakna dolga vlakna papir fizikalno-mehanske lastnosti cellulose fibres short fibres long fibres paper physical-mechanical properties true false false Slovenski jezik Angleški jezik Diplomsko delo/naloga 2026-08-29 09:00:09 2026-08-29 09:00:18 2026-08-30 04:15:35 0000-00-00 00:00:00 2026 0 0 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 1970-01-01 115400 29261.pdf 29261.pdf 1 F980AF774F925A6D54A59A07CCF9A9A7 07c3310979a47aa56676b13e4ea54e6bd5f36cae6022092ea789dbf0fa6e6ff8 e024e042-a376-11f1-9b0d-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=245418 Naravoslovnotehniška fakulteta 0 0 0