20.500.12556/RUL-185848 Vpliv procesnih parametrov na lasersko ablacijo polimerov ojačenih z ogljikovimi vlakni Effect of process parameters on laser ablation of carbon fiber reinforced polymers Diplomsko delo obravnava lasersko obdelavo kompozita iz ogljikovih vlaken in polimerne matrice (CFRP). Zaradi kompozitne sestave imata obe komponenti različne lastnosti, ki pomembno vplivajo na lasersko obdelavo. Med najpomembnejše sodijo toplotna prevodnost, optična absorptivnost ter temperatura tališča in vrelišča. Cilj naloge je bil preučiti vpliv obdelovalnih parametrov na lasersko ablacijo z uporabo galvanometrske skenirne glave. Med eksperimenti smo spreminjali valovno dolžino laserske svetlobe, število prehodov pri enaki vneseni energiji, dolžino laserskega bliska ter stopnjo prekrivanja laserskih peg. Rezultate eksperimentov smo ovrednotili z merjenjem toplotno vplivanega območja (HAZ), hitrosti odstranjevanja materiala in hrapavosti obdelane površine. Ugotovili smo, da večja absorpcija ultravijolične (UV) svetlobe omogoča enakomernejšo ablacijo polimerne matrice. Odstranjevanje matrice z infrardečo (IR) svetlobo je mogoče doseči z daljšimi laserskimi bliski, pri katerih se matrica upari zaradi prenosa toplote, kar pa hkrati povzroči povečanje toplotno vplivanega območja. This diploma thesis investigates the laser processing of carbon fiber reinforced polymer (CFRP) composites. Due to its composite structure, the constituent materials exhibit different properties that significantly influence the laser processing behavior. The most important of these properties include thermal conductivity, optical absorptivity, and the melting and boiling temperatures. The objective of this thesis was to investigate the influence of processing parameters on laser ablation using a galvanometer scanning system. During the experiments, the following parameters were varied: laser wavelength, the number of passes at constant input energy, laser pulse duration, and laser spot overlap. The experimental results were evaluated by measuring the heat-affected zone (HAZ), the material removal rate, and the surface roughness. The results showed that the higher absorptivity of ultraviolet (UV) radiation promotes more uniform ablation of the polymer matrix. Matrix removal using infrared (IR) radiation can be achieved with longer laser pulses, where the matrix is vaporized through heat transfer; however, this also results in an increase in the heat-affected zone. laser CFRP kompozit ablacija procesni parametri hrapavost površine toplotno vplivano območje laser CFRP composite ablation process parameters surface roughness heat affected zone true false false [Ž. Čampa] Slovenski jezik Angleški jezik Diplomsko delo/naloga 2026-08-21 08:32:38 2026-08-21 08:32:43 2026-08-22 04:19:33 0000-00-00 00:00:00 2026 0 Ljubljana 0 XXII, 58 f. 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 544.537:665.652.2(043.2) 288107 288487171 48533.pdf 48533.pdf 1 BF26EF32CDFF747081530984481985D1 ccbf7d7d42326c0a0e042f5616f058f50d0ce64e3a30afca1dd9ae6105d959fa b91f8346-9d29-11f1-9b0d-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=244837 Fakulteta za strojništvo 0 0 0