20.500.12556/RUL-180503 Self-lubricant TiAl(V)N films for high temperature applications: a comparative study of monolithic and multilayer films architectures TiAl(V)N coatings with increasing V content were deposited using DC magnetron sputtering in both monolithic and multilayer (TiAlN/TiAl(V)N) architectures to assess the effect of V impact and film architecture on mechanical, oxidation, and tribological behaviour. Monolithic and multilayer coatings showed similar morphology regardless of the V concentration and the coating architecture. The oxidation resistance of the multilayer coatings is better than that of the monolithic coatings since, in the former case, the presence of the TiAlN layers allows the formation of a more protective oxide layer, rich in Al▫$_{2}$▫O▫$_{3}$▫. Similarly, the multilayer configuration enhanced the tribological performance of the coatings, showing a progressive reduction in friction and greater wear resistance compared to both the reference and corresponding monolithic coatings, particularly at elevated temperatures. TiAl(V)N films self-lubricant films multilayer oxidation tribology TiAl(V)N premazi samomazalne folije večplastni premazi oksidacija tribologija true false true Angleški jezik Slovenski jezik Članek v reviji 2026-03-11 04:38:14 2026-05-15 09:05:07 2026-05-16 04:59:40 0000-00-00 00:00:00 2026 0 0 Str. 2143-2152 Vol. 41 2026 0000-00-00 Zaloznikova Objavljeno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 539.92:621.89 2238-7854 10.1016/j.jmrt.2026.01.116 271167747 Cavaleiro,_Yaqub_..._Self-lubricant....pdf Cavaleiro,_Yaqub_..._Self-lubricant....pdf 1 C53170E377A11D1EBEE16FC69092BFB3 7698b04f2ef9b0959a22bbd53d6b098cc0b39f3618898e13470417cbffed0349 ea4ae080-1d22-11f1-a1ba-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=230010 https://www.sciencedirect.com/science/article/pii/S223878542600116X 1 5211e725-1cfb-11f1-a1ba-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=229953 Fakulteta za strojništvo 0 0 0