20.500.12556/RUL-174671 Mutually enhanced mechanical and tribological properties in magnetron sputtered ▫$Mo_{2}N/Ag-SiN_{x}$▫ self-lubricating multilayered films via epitaxial growth design Achieving simultaneous enhancement of both mechanical and self-lubricating properties by incorporating soft lubricants into nitride films has been a longstanding challenge in the development of solid lubricant materials. This paper introduced a novel approach to overcome this challenge by developing coherent-structured ▫$Mo_{2}N/Ag-SiN_{x}$▫ multilayered films using radio frequency (RF) magnetron sputtering. The multilayer films were designed with a fixed modulation period of 30 nm, while the modulation ratio (γ) was varied from 1:9 to 1:1. The ▫$Mo_{2}N$▫ layers exhibited a single ▫$fcc-Mo_{2}N$▫ phase, while the ▫$Ag-SiN_{x}$▫ layers formed a dual-phase structure comprising fcc-Ag nanoparticles embedded in an amorphous ▫$SiN_{x}$▫ matrix. At a modulation ratio of 1:9, the ▫$Ag-SiN_{x}$▫ layer epitaxially grew on the ▫$Mo_{2}N$▫ template, resulting in a coherent structure. This coherent structure significantly enhanced both the hardness and elastic modulus, reaching approximately 36 GPa and 230 GPa, respectively. The improved wear resistance at room temperature can be attributed to the coherent strengthening effect, which not only elevated the film's hardness but also eliminated sharp interfaces between modulation layers, thereby reducing crack initiation sites. In temperature-cycling tribo-testing from room temperature to 600 °C, the film with a γ of 1:9 maintained a stable coefficient of friction around 0.2, except during the initial room temperature, where it was 0.4. The wear rate could not be accurately calculated due to the adhered tribolayer on the top of the wear track following the initial tribo-test at 600 °C. The excellent tribological properties across temperature cycles were attributed to the synergistic lubricant characteristics of both layers and the formation of self-lubricating tribo-phases. The optimized ▫$Mo_{2}N/Ag-SiN_{x}$▫ multilayered films provide an effective balance of lubrication and mechanical stability under extreme conditions, making them highly promising for high-performance engineering applications. magnetron sputtering multilayered films coherent strengthening mechanical properties tribological properties magnetronsko naprševanje večplastne folije koherentno utrjevanje mehanske lastnosti tribološke lastnosti true false true Angleški jezik Slovenski jezik Članek v reviji 2025-10-08 12:26:01 2025-10-08 12:26:08 2025-11-27 03:31:56 0000-00-00 00:00:00 2025 0 0 Str. 43924-43932 issue 25, pt. A Vol. 51 Oct. 2025 0000-00-00 Zaloznikova Objavljeno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 539.92:531.43 0272-8842 10.1016/j.ceramint.2025.07.123 252286467 Luan,_Kalin_..._Mutually_enhanced....pdf Luan,_Kalin_..._Mutually_enhanced....pdf 1 A2AC952ACBB0341EC4A9E7361EA4DB9E bb7ef1ac10733cd4d62eba9ca98073010000ffb96836cbe71821745fa87e8b5d 641c149a-a431-11f0-9328-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=219539 https://www.sciencedirect.com/science/article/pii/S0272884225033449 1 f91619e6-a430-11f0-9328-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=219533 Fakulteta za strojništvo 0 0 0