20.500.12556/RUL-172550 Primerjava hidrotermalne metode in mikrovalovnega razkroja (ekstrakcije) za pripravo alternativnih alkalijskih aktivatorjev Comparison of the hydrothermal method and microwave digestion (extraction) for the preparation of alternative alkaline activators Emisije ogljikovega dioksida (CO$_2$) predstavljajo velik okoljski izziv, pri čemer cementna industrija prispeva približno 8 % vseh globalnih emisij. Zaradi potrebe po zmanjšanju ogljičnega odtisa je iskanje alternativ, ki bi lahko delno ali v celoti nadomestile uporabo cementa, izredno pomembno. Ena izmed perspektivnih rešitev so alkalijsko aktivirani materiali (AAM), ki predstavljajo potencialno okoljsko sprejemljivejšo zamenjavo za portlandski cement. Za njihovo pripravo potrebujemo alkalijski aktivator in mineralni odpadek (prekurzor). Trenutno se kot komercialni aktivatorji najpogosteje uporabljajo natrijev oz. kalijev silikat in hidroksidi. Tudi pri izdelavi aktivatorjev nastajajo precejšnje emisije CO$_2$. Namesto tega bi lahko uporabili alternativne alkalijske aktivatorje (AAA). Ti so narejeni iz odpadkov, ki vsebujejo velik delež silicija (Si). Mi smo AAA pripravili iz odpadnega stekla (WG), steklene volne (GW), kamene volne (SW), steklene volne brez veziva (GWc), kamene volne brez veziva (SWc) in mikrosilike (MS). Za alkalen medij smo uporabili različne raztopine natrijevega (NaOH) in kalijevega (KOH) hidroksida. Za njihovo pripravo smo uporabili dve različni metodi, hidrotermalno metodo ter mikrovalovni razkroj – ekstrakcija. Sledilo je določanje koncentracij Si in Al s pomočjo induktivno sklopljene plazme z optično emisijsko spektroskopijo (ICP-OES) in identifikacija prisotnih funkcionalnih skupin z infrardečo spektroskopijo s Fourierjevo transformacijo (FTIR). Nato smo iz AAA, ki so vsebovali najvišjo koncentracijo Si, pripravili mešanice, da smo dobili AAM. Za prekurzor smo uporabili metakaolin (MK) in metalurško žlindro (BFS). Sledilo je merjenje tlačne in upogibne trdnosti. Izbrane AAM smo tudi pogledali z vrstičnim elektronskim mikroskopom (SEM) in primerjali njihovo mikrostrukturo z mehanskimi lastnostmi in koncentracijami Si v uporabljenih AAA. Carbon dioxide (CO$_2$) emissions represent a major environmental challenge, with the cement industry contributing around 8% of total global emissions. The necessity to reduce the carbon footprint makes the search for alternatives that can partially or fully replace the use of cement of paramount importance. One perspective solution is alkali activated materials (AAMs), which represent a potentially more environmentally acceptable substitute for Portland cement. To prepare them, you need an alkali activator and mineral waste (precursor). Currently, sodium or potassium silicate and hydroxides are the most used commercial activators. Again, the production of these activators generates substantial CO$_2$ emissions. Alternative alkaline activators (AAA) can be used instead. These are made with waste which contains a high proportion of silica (Si). We prepared AAA from waste glass (WG), glass wool (GW), stone wool (SW), glass wool without binder (GWc), stone wool without binder (SWc) and microsilica (MS). Different solutions of sodium (NaOH) and potassium (KOH) hydroxide were used as the alkaline medium. Two different methods were used for their preparation, hydrothermal method and microwave digestion-extraction. This was followed by the determination of Si and Al concentrations by inductively coupled plasma optical emission spectroscopy (ICP-OES) and determination of functional groups present in the samples by Fourier transform infrared spectroscopy (FTIR). Mixtures were then prepared from the AAAs containing the highest Si concentrations to produce AAM. Metakaoline (MK) and metallurgical slag (BFS) were used as precursors, which were followed by compressive and flexural strength measurements. The selected AAMs were also looked at with a scanning electron microscope (SEM) and their microstructure was compared with the mechanical properties and Si concentrations of the AAAs used. alternativni alkalijski aktivatorji – AAA hidrotermalna metoda mikrovalovni razkroj – ekstrakcija alkalijsko aktivirani materiali – AAM Alternative alkaline activators (AAA) hydrothermal method microwave digestion-extraction alkali activated materials (AAMs). true false false Slovenski jezik Angleški jezik Magistrsko delo/naloga 2025-09-08 13:30:00 2025-09-08 13:30:07 2025-10-24 12:26:06 0000-00-00 00:00:00 2025 0 0 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 24124 254660611 Zupancic_Kaja_-_Primerjava_hidrotermalne_metode_in_mikrovalovnega_razkroja_(ekstrakcije)_za_prip.pdf Zupancic_Kaja_-_Primerjava_hidrotermalne_metode_in_mikrovalovnega_razkroja_(ekstrakcije)_za_prip.pdf 1 15867D5C1D732F1AF00553401FC318E9 fedb21da8d220672fb1241bd5a969cb2911022a1ee00b4611ab7c6819810b48c 0586b5eb-8ca7-11f0-9328-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=216383 Fakulteta za kemijo in kemijsko tehnologijo 0 0 0