20.500.12556/RUL-162087 Časovno odvisno spreminjanje akustičnih lastnosti površinsko obdelanih lesenih resonančnih plošč Time dependent variation of the acoustic properties of coated wood resonant panels V diplomskem delu smo spremljali časovno odvisno spreminjanje akustičnih lastnosti pri smrekovih (Picea abies (L.) Karst.) ter javorjevih (Acer pseudoplatanus (L.)) lamelah dimenzij 400 mm × 80 mm × 3 mm, premazanih s celulozno-nitratnim ali poliuretanskim premaznim sistemom. Akustične lastnosti smo proučevali z merjenjem frekvenčnega odziva ob dinamično mehanskem vzbujanju, pri prečnem nihanju. Meritve smo izvedli na neobdelanih lamelah ter po površinski obdelavi še sedemkrat, najprej štirikrat z razmikom enega tedna, nato pa še trikrat z razmikom enega meseca. Po nanosu premaznih sistemov se je značilno povečala gostota preizkušancev, prav tako pa je izrazito narastlo tudi dušenje zvoka (tanδ). Prišlo je tudi do padca lastne frekvence (f), dinamičnega modula elastičnosti (E) ter drugih akustičnih kazalnikov (ACE, RACE, Esp). Trdota celulozno-nitratnega ter poliuretanskega premaznega sistema je v postopku staranja narasla za od 50 % vse do 120 % po 1,5 meseca staranja. Časovno odvisno utrjevanje premaznih sistemov vpliva na nižanje dušenja zvoka (tanδ), kjer po 1,5 meseca dosežemo za do 50 % nižje vrednosti dušenja zvoka, ki se približujejo vrednostim površinsko neobdelanega lesa. Pri dinamičnemu modulu elastičnosti površinsko obdelanih resonančnih plošč nismo zabeležili bistvenih sprememb, le v rangu ±10 %. Zaradi časovno odvisnega zmanjšanja dušenja zvoka (tanδ) je s postopkom staranja celulozno-nitratnega ter poliuretanskega premaza prišlo do značilnega povečanja drugih akustičnih kazalnikov (ACE, RACE, K), saj je pri slednjih dušenje zvoka neodvisna spremenljivka v imenovalcu. Po 1,5 meseca staranja premazov se kazalniki stabilizirajo ter dosežejo vrednosti, ki so primerljive s površinsko nezaščitenimi lesenimi resonančnimi ploščami. In this diploma, the change of acoustic properties over time of spruce (Picea abies (L.) Karst.) and maple (Acer pseudoplatanus (L.)) lamellae with the dimensions of 400 mm × 75 mm × 3 mm, and treated with a cellulose-nitrate or polyurethane coating, were investigated. The acoustic properties were investigated by studying the frequency response of the flexural vibration mode after dynamic-mechanical excitation of the lamellae. The tests were first conducted on untreated lamellae and repeated seven times on treated samples – four times a week apart, and three times a month apart. After the application of surface coatings, the density of the lamellae increased significantly, and the sound damping (tanδ) rose sharply. A drop in resonant frequency (f), the dynamic modulus of elasticity (E) and other acoustic properties (ACE, RACE, Esp) was also detected. In the process of ageing, the hardness of both cellulose-nitrate and polyurethane coatings rose by about 50% up to 120% in 1.5 months. The hardening process of the coatings influences sound damping (tanδ), lowering it by about 50% in 1.5 months, with measurements close to those obtained on lamellae without a surface coating. The dynamic modulus of elasticity did not change much with time, as it stayed well within the ±10% range. The reduction of sound damping (tanδ) as the coatings aged caused a rise in the other acoustic properties (ACE, RACE, K) that are directly dependent on tanδ. The aforementioned acoustic properties stabilized and reached values comparable to untreated lamellae in 1.5 months. les površinska obdelava akustične lastnosti časovna odvisnost wood surface finishing acoustic properties time dependance true false false [J. Vadnjal May] Slovenski jezik Angleški jezik Diplomsko delo/naloga 2024-09-19 07:15:40 2024-09-19 07:15:49 2024-10-03 09:09:14 0000-00-00 00:00:00 2024 0 0 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 630*829.1:812.12 245794 210002179 DIP_Vadnjal_May_Jakob_2024.pdf DIP_Vadnjal_May_Jakob_2024.pdf 1 6AE232B378F959B8F560BE1ED8CBFFCF ee3508914ee66bff95ea808c5affa8f1635ac6fcd525b33257f676d0fb06ee69 2057112b-7646-11ef-b232-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=191241 Biotehniška fakulteta 0 0 0