20.500.12556/RUL-156365 Effect of multi-scale fillers on the tribological behavior of UHMWPE composites in water-lubricated contacts This study investigates the impact of graphite, hexagonal boron nitride and short carbon fibers, acting as micro- and nano-fillers, on the tribological performance of ultra-high-molecular-weight polyethylene (UHMWPE) hybrid composites. The tribological performance is evaluated under boundary-lubrication conditions with distilled water at contact pressures in the range from 5 and 15 MPa. The fillers were found to work synergistically, with the best performance recorded when the compositions incorporated fillers of all scales. The most effective composite, consisting of short carbon fibers, micro-scale graphite, micro-scale hBN and nano-scale hBN, reduced the coefficient of friction by 75 %, reaching a value of 0.06, and the specific wear rate by two orders of magnitude to 2 × 10$^{−7}$ mm$^3$/Nm, compared to pure UHMWPE. The fillers’ size also played an important role. Composites with nano-boron nitride led to 40 % lower friction compared to micro-scale fillers only. However, all the fillers reduced the amount of abrasive wear, especially the boron nitride, as a consequence of the tribochemical reaction between the boron nitride and water at the interface. Additionally, the formation of a transfer film was observed on the steel discs, with only short carbon fibers and graphite contributing to its formation from among the fillers used. multi-scale fillers UHMWPE composites water tribology večplastnost polnila UHMWPE kompoziti voda tribologija true false true Angleški jezik Slovenski jezik Članek v reviji 2024-05-22 09:28:53 2024-05-22 09:28:54 2024-05-29 04:02:27 0000-00-00 00:00:00 2024 0 0 18 str. Vol. 196, art. 109669 Aug. 2024 0000-00-00 Zaloznikova Objavljeno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 539.92 0301-679X 10.1016/j.triboint.2024.109669 196211459 1-s2.0-S0301679X24004213-main.pdf 1-s2.0-S0301679X24004213-main.pdf 1 1C5BD2DC8B777B0B16E282634505BC86 f9052b4cb1470ec1ff15250e114690d42466b23a033281a7af21b27371dbbfaa 40fac6a1-1cd0-11ef-a9a3-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=185668 https://www.sciencedirect.com/science/article/pii/S0301679X24004213 1 f292ea8a-180c-11ef-b91f-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=183787 Fakulteta za strojništvo 0 0 0