20.500.12556/RUL-156343 Sustainable in situ synthesis of silver/titanium dioxide/organofunctional trialkoxysilane nanocomposite coatings on cotton fabric to tailor superior multifunctional protective properties Multifunctional properties are crucial for the production of high-quality technical textiles. In this study, a cotton fabric with simultaneously superior UV-protection, self-sterilisation, photocatalytic self-cleaning and flame retardant properties was produced using a sol–gel/hydrothermal process, in which titanium(IV) isopropoxide (TTIP) as a titanium dioxide (TiO$_2$) precursor was combined for the first time with mixtures of organofunctional trialkoxysiloxanes, i.e., 3-(trihydroxysilyl)propyl methylphosphonate (TPMP) as a P-based flame retardant and dimethyloctadecyl [3-(trimethoxysilyl)propyl]ammonium chloride (SiQAC) or aminopropyltriethoxysilane (APTES) as the antimicrobial, biobarrier-forming precursors. The latter was used in two increased concentrations of APTES1 and APTES2. A sol–gel/hydrothermal approach was employed with a small amount of silver nitrate (AgNO$_3$) added during the hydrothermal treatment to produce Ag-loaded TiO$_2$. The results of scanning electron microscopy (SEM), energy-dispersive X-ray analysis (EDS), X-ray diffraction spectroscopy (XRD), inductively coupled plasma mass spectroscopy (ICP MS) and Fourier-transform infrared spectroscopy (FT-IR) confirmed the successful functionalisation of TiO$_2$ by TPMP, SiQAC and APTES through the formation of Si–O–Ti bonds and the well-dispersed Ag/TiO$_2$/TPMP/SiQAC, Ag/TiO$_2$/TPMP/APTES1 and Ag/TiO$_2$/TPMP/APTES2 coatings on the surface of the cotton fabric. The type of biobarrier-forming precursor significantly influenced the formation of the Ag species after the Ag loading of TiO$_2$. The presence of SiQAC induced the formation of AgCl crystals, while APTES controlled the formation of silver nanoparticles (Ag NPs), which was more pronounced at the lower APTES1 concentration. The interactions between the coating components significantly influenced the functional protection performance, with the highest level of cooperation achieved in the Ag/TiO$_2$/TPMP/SiQAC and Ag/TiO$_2$/TPMP/APTES1 coatings, which exhibited the best overall multifunctionality, albeit with certain drawbacks. While the Ag/TiO$_2$/TPMP/APTES1 coating provided excellent UV protection for the cotton, this was only improved by the Ag/TiO$_2$/TPMP/SiQAC coating. At the same time, the Ag/TiO$_2$/TPMP/APTES1 coating impaired the development of the char barrier by TPMP, which is due to the formation of Ag NPs. Nevertheless, both coatings showed high photocatalytic self-cleaning performance, complete self-sterilisation activity and improved burning behaviour. cotton fabric titanium dioxide TiO$_2$ silver loading Ag organofunctional trialkoxysilanes surface functionalization multifunctional properties bombažna tkanina titanov dioksid TiO$_2$ srebro Ag organofunkcionalni trialkoksisilani funkcionalizacija površine večfunkcionalne lastnosti true false true Angleški jezik Slovenski jezik Članek v reviji 2024-05-21 09:39:21 2024-05-21 09:39:22 2024-08-28 13:17:57 0000-00-00 00:00:00 2024 0 0 16 str. Vol. 49, art. 104447 2024 0000-00-00 Zaloznikova Objavljeno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 677 2468-0230 10.1016/j.surfin.2024.104447 195811075 1-s2.0-S2468023024006047-main.pdf 1-s2.0-S2468023024006047-main.pdf 1 6F09324074361A8B89CD7C2EA7D780B0 ad532db89324f3f4fd959c052b969499c6666c2256048968001e86fcec54848a 99574e11-1745-11ef-b8e5-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=183756 https://www.sciencedirect.com/science/article/pii/S2468023024006047 1 3e5e6325-1745-11ef-b8e5-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=183755 Naravoslovnotehniška fakulteta Fakulteta za kemijo in kemijsko tehnologijo 0 0 0