20.500.12556/RUL-156 Sorpcijske lastnosti lesa zaščitenega z bakrovimi pripravki ali termično modifikacijo v vakuumu diplomsko delo (visokošolski strokovni študij) Sorption properties of copper treated wood or thermally modified wood in vacuum graduation thesis (higher professional studies) Za določitev sorpcijskih lastnosti zaščitenega lesa smo izdelali vzorce iz smrekovine. Del vzorcev smo vakuumsko impregnirali s pripravki na osnovi bakrovega(II) sulfata in etanolamina (CuS, CuSEA, CuSEAQBOK) 2 različnih koncentracij, ostale pa termično modificirali pri 180 °C, 195 °C, 210 °C, 225 °C, 240 °C. Vse vzorce smo izpostavili 5 klimam z različno relativno zračno vlažnostjo (33 %, 44 %, 65 %, 88 %, 98-100 %) ter izračunali adsorpcijske in desorpcijske krivulje. Na povečano higroskopnost vzorcev poleg bakrovega(II) sulfata in etanolamina dodatno vplivajo še ostale komponente: bor, kvartarna amonijeva spojina in oktanojska kislina. Pri vseh klimah izpostavitve imajo vsi termično modificirani vzorci nižje ravnovesne vlažnosti kot pa kontrolni in neobdelani vzorci.Ugotovili smo, da so pri termični modifikaciji sorpcijske lastnosti v tesni povezavi z izgubo mase. Višja kot je, večja je izguba mase; posledično je manjša tudi ravnovesna vlažnost vzorcev in s tem dovzetnost za higroskopičnost. To elucidate sorption properties of preserved wood, Norway spruce wood specimens were prepared. One half of the specimens was treated with copper(II)sulphate and ethanolamine based wood preservatives (CuS, CuSEA, CuSEAQBOK) of 2 different concentrations, and the other modified at 180 °C, 195 °C, 210 °C, 225 °C, 240 °C. All the specimens were exposed in chambers with different air humidity (33 %, 44 %, 65 %, 88 %, 98-100 %). Afterwards, adsorption and desorption curves were calculated. Results indicate that besides copper(II) sulphate and ethanolamine other components of preservative solution like boron, quaternary ammonium compound and octanoic acid, have influence on increased hygroscopic properties of impregnated wood. On the other, all thermally modified specimens exhibited lower equilibrium moisture in comparison to control unmodified wood. There is a significant correlation between sorption properties and mass losses caused by thermal treatment. Higher temperatures of modification result in higher mass losses, what is reflected in lower equilibrium moisture content and hygroscopic properties. les zaščita lesa baker amini modifikacija sorpcija desorpcija vlažnost lesa wood wood preservation copper amine modification sorption desorption moisture content true false false [M. Vavkman] Slovenski jezik Angleški jezik Diplomsko delo 2014-07-11 12:24:23 2014-07-11 12:24:23 2022-07-11 10:07:22 0000-00-00 00:00:00 2006 0 Ljubljana 0 XIV, 58 f., [20 f. pril.] 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 630*841 1453705 vs_vavkman_marko.pdf vs_vavkman_marko.pdf 1 F69DFA1EF5173B8C0A80C9754587D7DC 7753c9483f7b3862410410d2f6b7f7be0a1bc05cfba56e2a028e50847c327e69 56a7f7af-a1b9-11eb-a523-00155dcfd717 20.500.12556/rul/0ad7ca2e-d9e3-471f-824b-8957db84d84f https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=132208 Biotehniška fakulteta 0 0 0