20.500.12556/RUL-151023 Utrjevanje historičnih materialov z utrjevalci na osnovi kalcijevega hidroksida in kalcijevega acetoacetata Consolidation of historic materials with consolidants based on calcium hydroxide and calcium acetoacetate Kulturna dediščina je neprecenljiva vrednost nekega kraja ali države. Predmeti kulturne dediščine so podvrženi raznim procesom staranja in degradacije, kar vodi v njihovo propadanje. Zato uporabljamo utrjevanje, ki je eden ključnih postopkov ohranjevanja, ki ga ti predmeti potrebujejo, da preživijo v času. Pri procesu utrjevanja uporabljamo utrjevalce, to so različna veziva, razpršena v topilu, ki se nanesejo na propadajočo plast materialov, da se obnovi izgubljena kohezija med delci. Utrjevalci na osnovi Ca(OH)2 so zaradi svoje kemijske združljivosti z objekti na osnovi karbonata eden najbolj uporabljenih materialov pri utrjevanju. Med najbolj obetavnimi utrjevalci na osnovi Ca(OH)2 so nanodelci Ca(OH)2. Utrjevanje z nanodelci temelji na reakciji karbonatizacije. Med karbonatizacijo Ca(OH)2 delci reagirajo s CO2 iz zraka, kar vodi do nastanka CaCO3. Ta poveže ohlapne delce in zapolni razpoke; s tem utrdi razpadajočo porozno snov. Utrjevanje z nanodelci se je izkazalo zelo učinkovito za površinsko utrjevanje. Komercialna izdelka na osnovi nanodelcev sta CaloSil® in Nanorestore®, ki sta bila uporabljena pri različnih študijah in projektih. Kljub vsem dobrim lastnosti se pojavljajo težave, ko je potrebno globinsko utrjevanje. Zato je bila v okviru projekta HEROMAT razvita vodna raztopina kalcijevega acetoacetata – Ca(OAcAc)2, tudi CFW (Consolidant formulation water). Kalcijev acetoacetat v prisotnosti vode razpade do kalcijevega karbonata, ogljikovega dioksida in acetona. Utrjevalni učinek je dosežen, ko CO2 in aceton izhlapita in novonastali delci CaCO3 zapolnijo poškodovano podlago. CFW je v primerjavi z nanodelci pokazala večje prodiranje v podlago, manjše število nanosov, boljše izboljšanje mehanskih lastnosti ter ni imela večjega vpliva na barvo. Cultural heritage is the priceless value of a place or a country. Cultural heritage objects are subject to various aging and degradation processes that lead to a deterioration of their quality. For this reason, we resort to consolidation which is one of the most important conservation procedures that these objects need to survive over time. Consolidation involves the use of consolidants which are various binders dispersed in a solvent that is applied to the damaged layer of the materials to restore the lost cohesion between the particles. Ca(OH)2-based consolidants are one of the most commonly used materials for consolidation due to their chemical compatibility with carbonate-containing objects. Among the most promising Ca(OH)2-based consolidants are Ca(OH)2 nanoparticles. Consolidation with nanoparticles is based on a carbonation reaction. During carbonation, Ca(OH)2 particles react with CO2 from the air resulting in the formation of CaCO3. This binds the loose particles and fills the cracks solidifying the porous material. Nanoparticle consolidation is very effective for surface consolidation. Commercial nanoparticle-based products include CaLoSil® and Nanorestore®, which have been used in various studies and projects. Despite all their good properties, problems arise when deep consolidation is required. For this purpose, an aqueous solution of calcium acetoacetate – Ca(OAcAc)2, also known as CFW (Consolidant Formulation Water) – was developed as part of the HEROMAT project. Calcium acetoacetate decomposes in the presence of water to calcium carbonate, carbon dioxide, and acetone. The consolidation effect is achieved when CO2 and acetone evaporate and the newly formed CaCO3 particles fill the damaged substrate. CFW penetrates better into the substrate, needs to be applied less often, improves mechanical properties, and has no significant effect on color compared to nanoparticles. utrjevanje kalcijev hidroksid kalcijev acetoacetat consolidation calcium hydroxide calcium acetoacetate true false false Slovenski jezik Angleški jezik Diplomsko delo/naloga 2023-09-27 11:50:00 2023-09-27 11:50:00 2023-11-23 12:08:19 0000-00-00 00:00:00 2023 0 0 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 22925 173413123 Valencic_Ana_-_Utrjevanje_historicnih_materialov_z_utrjevalci_na_osnovi_kalcijevega_hidroksida_i.pdf Valencic_Ana_-_Utrjevanje_historicnih_materialov_z_utrjevalci_na_osnovi_kalcijevega_hidroksida_i.pdf 1 5755F337F8EDCEB26902DF909A6DF4A4 97a298f74dd076276e39f0930004d5f3e7375e7843b6bfeb0007a65e28f0f0b0 3a8ffce9-5d1b-11ee-a9d7-0050569b8976 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=175904 Fakulteta za kemijo in kemijsko tehnologijo 0 0 0